Evolution of Iron-Rich Intermetallics and its Effect on the Mechanical Properties of Al-Cu-Mn-Fe-Si Alloys after Thermal Exposure and High-Temperature Tensile Testing

Bo Lin,xiangxiang he,Yuliang Zhao,Rui Xu,Yemao Lu
DOI: https://doi.org/10.2139/ssrn.4132121
2022-01-01
SSRN Electronic Journal
Abstract:Si addition is commonly used to modify the iron-rich intermetallics in Al-Cu-Mn-Fe alloys, which is beneficial to increasing the use of recycled aluminum. Most of the available research has focused on the effect of Si content on the room-temperature mechanical properties of Al-Cu-Mn-Fe alloys. To expand the application of Al-Cu-Mn-Fe-Si alloys as light heat-resistant structural components in the automotive and aerospace industries, it is of great importance to investigate the evolution of iron-rich intermetallics and its effect on the fracture behavior of Al-Cu-Mn-Fe-Si alloys after thermal exposure and high-temperature tensile testing. In this work, the evolution of iron-rich intermetallics and the high-temperature mechanical properties of heat-treated Al-6.5Cu-0.6Mn-0.5Fe alloys with different Si contents after thermal exposure and high-temperature tensile testing were assessed by tensile tests, image analysis, scanning electron microscopy, X-Ray diffraction, transmission electron microscopy, and atomic probe tomography. The results indicate that the Al-6.5Cu-0.6Mn-0.5Fe-0.1Si alloy has excellent and stable high-temperature mechanical properties after long thermal exposure, which are better than those of most heat-resistant Al alloys. The high performance of the high-temperature mechanical properties is attributed to the high heat resistance of secondary intermetallics and precipitated particles. The addition of Si is detrimental to the strength of Al-6.5Cu-0.6Mn-0.5Fe alloys after long thermal exposure. This can be attributed to the solid-state phase transformation of iron-rich intermetallics from α-Fe to β-Fe, which results in the increase of needle-like Fe-rich phases and Si particles, the agglomeration of secondary intermetallics, and the consumption of Al2Cu phases. This result implies that Si is not suitable for modifying the iron-rich intermetallics in Al-Cu-Mn-Fe alloys used as light heat-resistant structural components.
What problem does this paper attempt to address?