A Novel Perovskite Electron–Ion Conductive Coating to Simultaneously Enhance Cycling Stability and Rate Capability of Li 1.2 Ni 0.13 Co 0.13 Mn 0.54 O 2 Cathode Material for Lithium‐Ion Batteries
Mingxi Gao,Chenhui Yan,Qinong Shao,Jian Chen,Chenyang Zhang,Gairong Chen,Yinzhu Jiang,Tiejun Zhu,Wenping Sun,Yongfeng Liu,Mingxia Gao,Hongge Pan
DOI: https://doi.org/10.1002/smll.202008132
IF: 13.3
2021-03-26
Small
Abstract:<p>Poor cycling stability and rate capability are two key issues needing to be solved for Li‐ and Mn‐rich oxide cathode material for lithium‐ion batteries (LIBs). Herein, a novel perovskite electron–ion mixed conductor Nd<sub>0.6</sub>Sr<sub>0.4</sub>CoO<sub>3</sub> (NSCO) is used as the coating layer on Li<sub>1.2</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>Mn<sub>0.54</sub>O<sub>2</sub> (LNCMO) to simultaneously enhance its cycling stability and rate capability. By coating 3 wt% NSCO, LNCMO–3NSCO exhibits an optimal cycling performance with a capacity retention of 99% at 0.1C (1C <b>=</b> 200 mA g<sup>−1</sup>) after 60 cycles, 91% at 1C after 300 cycles, and 54% at 20C after 1000 cycles, much better than 78%, 63%, and 3% of LNCMO, respectively. Even at a high charge and discharge rate of 50C, LNCMO–3NSCO exhibits a discharge capacity of 53 mAh g<sup>−1</sup> and a mid‐point discharge voltage of 2.88 V, much higher than those of LNCMO (24 mA h g<sup>−1</sup> and 2.40 V, respectively). Benefiting from the high electronic conductivity (1.46 S cm<sup>−1</sup>) and ionic conductivity (1.48 <b>×</b> 10<sup>−7</sup> S cm<sup>−1</sup>), NSCO coating not only suppresses transition metals dissolution and structure transformation, but also significantly enhances electronic conductivity and Li<sup>+</sup> diffusion coefficient of LNCMO by an order of magnitude.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology