Abstract:High belite sulphoaluminate cement (HBSC) has shown great potential as new lower CO2 footprint cementitious material. It makes sense to improve the hydrophobic property of HBSC to obtain high durability performance. In this paper, nontoxic short carbon chain lauric acid (LA) is used to match the early strength characteristic of HBSC to prepare fast-setting and eco-friendly LA-modified HBSC mortar (M-HBSCM). Sands modified with LA provide low surface energy for an integral hydrophobic effect. M-HBSCM exhibits superhydrophobicity even after hammering to expose the fractured internal structure, with a contact angle of 153.2°. And it shows outstanding self-cleaning property against contaminants such as sand and wet mud and a reduction in water absorption to around 23% of the ordinary HBSCM (O-HBSCM). The fabricated M-HBSCM has fast-setting property with an initial setting time of 29 min and a final setting time of 36 min. The abrasion test displays that the scratched area remains well superhydrophobic with high mechanical robustness when the droplets roll off on the inclined surface. Field-emission scanning electron microscope (FESEM) indicates that M-HBSCM contains more pores and coarser hydration products. The system of calcium alumina and pores exhibits a distinct hierarchical structure, providing the multilevel roughness required for the superhydrophobic surface. Fourier transform infrared (FTIR) spectrometer indicates that low surface energy functional groups have been successfully grafted onto M-HBSCM. The superhydrophobic concrete has good mechanical robustness, corrosion resistance, and fast-setting property, which can meet the demands of grouting reinforcement projects, the repair of various concrete structures, corrosion protection of marine structures and other projects.

Permeabilities and Mechanical Properties of Hardened Cement Pastes Modified with Sodium Laurate and Nano Silica

The Effect of Superhydrophobic Nano-Silica Particles on the Transport and Mechanical Properties of Hardened Cement Pastes

Effects of Multi-scale Siliceous Additives on Hydration and Microstructure of Hardened Cement Pastes

Fabricating hydrophobic silica fume to improve mechanical strength and anti-corrosion of integral hydrophobic cement mortar

Modification of water absorption and pore structure of high-volume fly ash cement pastes by incorporating nanosilica

Experimental study on strength and abrasion-resistance enhancement admixture

Effect of Nano-SiO2 on the Mechanical Properties, Microstructure, and Hydration Process of Cementitious Materials Incorporating Hydrophobic Admixture

Surface relaxation and permeability of cement pastes with hydrophobic agent: Combining 1H NMR and BET

Effect of Paraffin Oil Nanoemulsion As a Hydrophobic Modifier on Cement Paste Workability and Hydration

Effects and Mechanisms of Capric Acid/silica Capsule on Water Absorption Reduction of Cement Paste

Durability Improvement of Cement Using Amphiphilic Calcium Carbonate Nanoparticles

Extending the Modified Steel Slag Cement into the Hydrophobic and Anti-Icing Application

A fast-setting and eco-friendly superhydrophobic high belite sulphoaluminate cement mortar

Effects of Core-Shell Polycarboxylate Superplasticizer on the Fluidity and Hydration Behavior of Cement Paste

Effect of the Combined Treatment with Inorganic and Organic Agents on the Surface Hardening and Adhesion Properties of Cement-Based Materials

INVESTIGATING THE EFFECT OF NANO SILICA ON THE MECHANICAL PROPERTIES OF HARDENED CEMENT PASTE

Study on PVA-siloxane mixed emulsion coatings for hydrophobic cement mortar

Re-cementation Effects by Carbonation and the Pozzolanic Reaction on LWAs Produced by Hydrated Cement Paste Powder

Influence of silane on hydration characteristics and mechanical properties of cement paste

Mechanical properties and anti-efflorescence of cement-based coating containing silicon-aluminum based powder and modified-polyacrylate emulsion

Uncovering the role of hydrophobic silica fume (HPS) in rheology, hydration, and microstructure of ultra-high-performance concrete (UHPC)