Effect of Cr doping on Li2ZnTi3O8 as alternative anode material to enhance electrochemical properties of lithium-ion batteries

Anchali Jain,Amrish K. Panwar,Pawan K. Tyagi

DOI: https://doi.org/10.1007/s00339-022-05440-0

2022-03-15

Applied Physics A

Abstract:Cr-doped and undoped lithium zinc titanate (LZTO), Li2ZnCrxTi3−xO8 (x = 0, 0.1, 0.3, 0.5) has been prepared as alternative anode using a simple and facile high-temperature solid-state ball-milling route followed by calcination in the air atmosphere. The cubic spinel structure with P4332 space group is confirmed through X-ray Diffraction (XRD) for all compositions indicating doping of Cr3+ does not cause any changes within the lattice as well as maintain the phase structure up to an optimized doping. The study of morphology and distribution of the particles in the synthesized LZTO and doped LZTO compositions are carried out via scanning electron microscopy and transmission electron microscopy (TEM). It reveals the formation of polyhedron-shaped spherical facets in the sub-micron to nanometer range as observed by TEM. The particle size reduces toward the nanometer range as the amount of Cr doping increases and it also decreases the agglomeration of particles. All the samples doped with Cr indicate good electrochemical performance as compared to pristine LZTO. Sample Li2ZnCr0.3Ti2.7O8 doped with Cr content 0.3 displays higher discharge capacity, better cyclability, and lower polarization among all other Cr doped samples. Li2ZnCr0.3Ti2.7O8 delivered excellent rate performances attaining capacities of 251.73 ± 4, 184.34 ± 5, 157.42 ± 5, and 119.03 ± 4 mAh g−1 at 0.1C, 0.5C, 1, and 2C, respectively, which is higher than the pristine LZTO sample. Electrochemical impedance spectroscopy shows Li2ZnCr0.3Ti2.7O8 acquired a lower value of charge-transfer resistance and the fastest Li-ion diffusivity which enhances its capacity at higher current rates and makes it suitable as an alternative anode for lithium-ion batteries.