Abstract:<p>The focus of this work is to characterize the progressive damage and failure behavior of 2.5D woven alumina fiber reinforced silica ceramic matrix thin composite specimen under a planar tension-shear stress state. The tensile and shear stress-strain diagrams in the principal material coordinate system were obtained using the off-axis tension test with the digital image correlation technique. A mesoscale finite element model of the composite material was developed within the framework of continuum damage mechanics. The thickness effect on the macroscopic mechanical response was considered by removing the periodic boundary conditions along the thickness direction. The macroscopic stress-strain response given by the numerical model was validated by the experimental results. The interaction of the planar biaxial tension and shear stresses was taken into account in the model, quantified using a shear contribution coefficient in the modified 3D Hashin failure criterion. The results from the damage evolution analysis indicate that the linear tensile stress-strain response with a brittle fracture characteristic for the on-axis tension specimen is governed by the axial fiber bundle. The nonlinear tensile stress-strain response with the significantly reduced ultimate stress under biaxial tension and shear stress state results from multiple damages with evolution in both axial and transverse fiber bundles. Both the effective tensile modulus and the ultimate tensile strength increase with increasing the thickness of the specimen due to the increase of the fiber volume fraction. The strengthening induced by the size effect is less significant for the specimen under biaxial tension and shear stress state than that for the on-axis tension specimen owing to the involvement of shear response dominated by the matrix of the material. The results of this study provide new insight into the failure of 2.5D woven ceramic-based composite material, which contributes to the optimal design of the reusable thermal protection system structure.</p>

Progressive damage analysis and failure load of ceramic matrix composite hollow-shaft

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Progressive failure analysis of 2D woven composites at the meso-micro scale

Micro Failure Analysis of Fiber Metal Laminates

Micromechanics-based Progressive Failure Analysis of Carbon FIber/epoxy Composite Vessel under Combined Internal Pressure and Thermomechanical Loading

Development and validation of damage and failure models for the design of ceramic matrix composite components

Progressive Failure Analysis of Carbon Fiber/epoxy Composite Laminates Using Continuum Damage Mechanics

Progressive failure analysis of open-hole composite hoops under radial loading

Progressive fracture analysis of the open-hole composite laminates: experiment and simulation

Progressive damage analysis of double-layer variable thickness 3D woven composite scaled engine casing

A coupled ductile damage model for metal matrix composites: Development and application

Experimental and numerical investigation of progressive damage and failure behavior for 2.5D woven alumina fiber/silica matrix composites under a complex in-plane stress state

Three-dimensional progressive damage models for cohesively bonded composite π joint

Progressive failure analysis of perforated composite laminates considering nonlinear shear effect

A Monte Carlo simulation of damage and failure process with crack saturation for unidirectional fiber reinforced ceramic composites

Parametric Influences of Geometric Dimensions on High Temperature Mechanical Behaviors and Damage Mechanisms of Ceramic Matrix Composite and Superalloy Double Bolted Joints

Investigation on the Progressive Damage and Bearing Failure Behavior of Composite Laminated Bolted Joints under Tension

Development and experimental verification of an advanced 3D elastoplastic progressive damage model for composite materials

Constitutive model and failure criterion for orthotropic ceramic matrix composites under macroscopic plane stress

Damage Modeling of Oxide/oxide Ceramic Matrix Composites under Cyclic Loading Conditions

Progressive Damage and Failure Modeling in Fiber-Reinforced Laminated Composites Containing a Hole