Abstract:Wire arc additive manufacturing (WAAM) technology is widely used in the fields of aerospace, shipbuilding, and automobile industry due to the advantages of fast forming speed, high material utilization and low production cost. WAAM is extremely sensitive to parameters, and different processes and materials produce different deposition effects and properties. Therefore, it is of great significance to study the WAAM formability of various materials. Herein, the microstructure, mechanical properties, and galvanic corrosion behavior of the low-carbon high-strength steel (10CrNi3MoV) fabricated by cold metal transfer (CMT) WAAM technology were investigated. The single-channel multilayer deposition parts were prepared by reciprocating deposition, and the forming parts were divided into six zones by observing the different positions of the structure: matrix, heat-affected zone, remelting zone, initial deposition zone, interlayer zone, and interlayer bonding zone. Electron backscattered diffraction (EBSD) analysis showed that the amount of recrystallization and substructure in the deposition layer had no obvious change, and the texture phenomenon was the most obvious in the initial deposition zone of the pole map reaction. The texture phenomenon gradually weakened with the increase of the deposition layers. The microhardness from the matrix to the deposition stable zone was tested. The hardness of the matrix changed smoothly, that of the heat-affected zone was the largest, and that of the deposition layer was 221–282 HV0.2. The tensile properties were tested in different directions and angles, and the yield strength and tensile strength of the deposited layer were more than 550 MPa and 760 MPa, respectively. The galvanic corrosion behavior between the deposited layer and the matrix was investigated, and the polarization curve showed that the corrosion potential of the deposited layer was lower than that of the matrix, and the corrosion current density of the deposited layer was higher than that of the matrix.

Microstructure and Mechanical Properties of 800-MPa-Class High-Strength Low-Alloy Steel Part Fabricated by Wire Arc Additive Manufacturing

Microstructure and Mechanical Properties of 304L Steel Fabricated by Arc Additive Manufacturing

Mechanical Properties, Microstructural Characteristics and Heat Treatment Effects of WAAM Stainless-Steel Plate Material

Microstructure and Mechanical Properties of High-Strength, Low-Alloy Steel Thin-Wall Fabricated with Wire and Arc Additive Manufacturing

Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Fabricated by Wire and Arc Additive Manufacturing

Improving mechanical strength and isotropy for wire-arc additive manufactured 304L stainless steels via controlling arc heat input

Comparison of microstructural characteristics and mechanical properties of the high-strength low-alloy steels fabricated by wire arc additive manufacturing versus conventional casting

A Comparative Study of Microstructural Characteristics and Mechanical Properties of High-Strength Low-Alloy Steel Fabricated by Wire-Fed Laser Versus Wire Arc Additive Manufacturing

Effect of heat input on microstructural and mechanical properties of high strength low alloy steel block parts fabricated by wire arc additive manufacturing

Microstructure, Mechanical Properties, and Galvanic Corrosion of 10CrNi3MoV Fabricated by Wire Arc Additive Manufacturing

Microstructures and Fatigue Properties of High-Strength Low-Alloy Steel Prepared through Submerged-Arc Additive Manufacturing

Microstructure and mechanical properties of 600 MPa grade ultra-high strength aluminum alloy fabricated by wire-arc additive manufacturing

Mechanical properties and microstructure characteristics of wire arc additively manufactured high-strength steels

Enhanced High-Temperature Strength and Ductility of Wire Arc Additive Manufactured Al-Ce-Mg Alloys with Fine Α-Al/al11ce3 Eutectics

Microstructure and mechanical properties of high-strength low alloy steel by wire and arc additive manufacturing

The Fracture Toughness and Fatigue Crack Growth Properties of 18ni 300 Maraging Steel Manufactured by Wire + Arc Additive Manufacturing

Microstructure Evolution of Wire-Arc Additively Manufactured 2319 Aluminum Alloy with Interlayer Hammering

Microstructures and Mechanical Properties of Al–Zn–Mg Aluminium Alloy Samples Produced by Wire + Arc Additive Manufacturing

Microstructure and Properties of Additive Manufacturing by Gas-Shielded Arc Welding with Hydrogen-Resistant Steel Wires

Wire arc additive manufacturing of Al-Zn-Mg-Cu alloy: Microstructures and mechanical properties

Microstructure and Mechanical Properties of AlSi7Mg0.6 Aluminum Alloy Fabricated by Wire and Arc Additive Manufacturing Based on Cold Metal Transfer (WAAM-CMT)