Long-Term Creep Behavior of a CoCrFeNi Medium-Entropy Alloy

K. A. Rozman,M. Detrois,M. C. Gao,P. D. Jablonski,J. A. Hawk

DOI: https://doi.org/10.1007/s11665-022-06896-0

IF: 2.3

2022-04-25

Journal of Materials Engineering and Performance

Abstract:Current research shows that high-entropy alloys can offer superior oxidation resistance compared to more traditional austenitic stainless steels with equivalent tensile mechanical performance. While many reports have been published on creep of CoCrFeNiMn, few focus on the CoCrFeNi family of low- to medium-entropy alloys. In this manuscript, uniaxial tensile creep test results for more than 46,000 accumulated hours are presented on the equiatomic CoCrFeNi alloy. The alloy was manufactured at NETL using a vacuum induction melt solidification approach with a computationally designed homogenization cycle. After completing the homogenization cycle, the ingot was first hot-forged and then hot-rolled into 10-mm-thick plate, a product form that is relevant to many industries. Creep tests were performed in the temperature range of 600-650 °C using applied stresses from 120 to 189 MPa. This study builds upon previous results on the CoCrFeNiMn family of high-entropy alloys and offers a modicum of clarification about performance compared to small button melts by using ASTM standard test procedures and mechanical test specimens. The apparent creep activation energy and creep stress exponent were similar to those for CoCrFe medium-entropy and CoCrFeNiMn high-entropy alloys. The post-test creep microstructure showed some Cr segregation, which has also been noted for other CoCrFe alloys. The CoCrFeNi alloy also presents a double minimum or two minimum creep rate phenomena.

materials science, multidisciplinary