A comparative study of two C-containing high-entropy alloys Al0.3CrFeNi2 and Al0.3CoCrFeNi

Yao Lu,Kai Zhang,Bingbing Zhao,Xianping Dong,Lanting Zhang
DOI: https://doi.org/10.1016/j.msea.2022.143702
2022-09-15
Abstract:Two Al0.3CoCrFeNi and Al0.3CrFeNi2 high-entropy alloys (HEAs) containing ∼0.07% carbon were designed to explore the feasibility of replacing expensive Co with Ni. After aging at different temperatures (550, 700 and 900 °C), both alloys exhibited an excellent balance of strength and ductility, i.e. ultimate strength (>640 MPa) and elongation (>40%) at room temperature. Compared with the Al0.3CoCrFeNi HEA, the Al0.3CrFeNi2 alloy showed an increased volume fraction of L12 phase, the emergence of M23C6 and the elimination of B2 precipitation. The cost-effective Al0.3CrFeNi2 HEAs aged at 550 °C rendered a tensile yield strength of 245.8 MPa and an elongation of 22.4% at 700 °C compared with 151.8 MPa and 25.0% of the Al0.3CoCrFeNi. This increase of yield strength is attributed to the strengthening from the L12 precipitates. Thermodynamic calculation (Thermo-Calc) confirms the increased volume fraction of L12 phase in the HEA as the Ni content doubled. Calculated Gibbs energy of the M23C6 phase is systematically lower in the Al0.3CrFeNi2 explains the absence of M23C6 in the Co-containing Al0.3CoCrFeNi under similar heat treatment conditions. As the aging temperature increased, coarse M23C6 appeared at grain boundaries and reduced the high-temperature ductility of the Al0.3CrFeNi2 alloy.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
What problem does this paper attempt to address?