Abstract:In recent years, weight reduction of automobile bodies has been effective in reducing carbon dioxide emissions. For this reason, the replacement of steel, which has a large specific gravity, with aluminum alloys and carbon fiber reinforced plastics is being promoted for the right materials in the right places. In this case, an appropriate dissimilar material joining method is needed in terms of ease of assembly, joining performance, and cost. Friction stir welding (FSW) has emerged as a promising joining method for a variety of engineering applications. FSW is a solid-phase joining technique that has been shown to have significant advantages over conventional welding in terms of the strength and quality of the joints produced. However, during joining of metallic materials by FSW, microstructural changes may occur that affect their corrosion degradation. In this study, the corrosion behavior of A6061 jointed with high-strength steel (SPCC980) by FSW in aqueous NaCl solution and the effect of Al alloy microstructural changes on it were investigated. In this study, FSW was performed on A6061 and SPCC980 steel plates, and galvanic corrosion behavior was investigated by immersion tests and surface observations, as well as electrochemical measurements of Al alloys. Immersion tests were performed in 1 M NaCl solution. Micro electrochemical polarization tests of A6061 were also performed to investigate the corrosion behavior. In the immersion test of the galvanic couple of A6061 and SPCC980 steel plates in NaCl solution, galvanic corrosion occurred with the Al alloy as the anode and the steel plate as the cathode, and hydrogen evolution was observed mainly from the BM site on A6061 in the initial stage of immersion. This is due to the hydrogen evolution reaction occurring inside the pitting corrosion of the A6061. The pits was formed near Fe-rich inclusions in the BM site. In the HAZ site, corrosion propagated from Fe-rich inclusions along grain boundaries, but no pitting corrosion was formed. In the NZ site, minor localized corrosion was developed. These results indicate that the susceptibility to localized corrosion and its morphology differ in each site on the A6061. The difference in localized corrosion susceptibility on the A6061 was considered to be caused by the difference in the distribution of Fe-rich inclusions. However, the fact that the size and number of Fe-rich inclusions in each site did not differ suggests that the difference in anodic dissolution activity near Fe-rich inclusions affects pitting corrosion susceptibility in each site. A6061 alloy is a precipitation-strengthened Al alloy reinforced by β'' phase, which is a metastable phase of Mg 2 Si, and dense precipitation of β'' phase was observed in the BM site. Therefore, the reason for the higher localized corrosion susceptibility of BM is related to the precipitation of the β'' phase. This paper is based on results obtained from a project, JPNP14014, commissioned by the New Energy and Industrial Technology Development Organization (NEDO).

Galvanic corrosion behavior of friction stir welded AZ31B magnesium alloy and 6N01 aluminum alloy dissimilar joints

Corrosion Behavior of Joints of Mg-alloy AZ31 Fabricated by Friction Stir Welding

Microstructure characteristics and performance of dissimilar welds between magnesium alloy and aluminum formed by friction stirring

Microstructure, mechanical and corrosion behaviours in friction stir welding of dissimilar magnesium alloys

Microstructure and mechanical properties of dissimilar inertia friction welding of 7A04 aluminum alloy to AZ31 magnesium alloy

Mechanical properties and corrosion behaviour of dissimilar friction stir-welded Al 7075 and Mg AZ31 alloys with Cd and Zn interlayer

Corrosion Behavior of Al Alloy A6061 Jointed with High-Tensile Strength Steel By Friction Stir Welding in NaCl Solution

Influence of the Zn interlayer on the mechanical strength, corrosion and microstructural behavior of friction stir-welded 6061-T6 aluminium alloy and AZ61 magnesium alloy dissimilar joints

Assessment of the Corrosion Behavior of Friction-Stir-Welded Dissimilar Aluminum Alloys

Macro-galvanic Effect and Its Influence on Corrosion Behaviors of Friction Stir Welding Joint of 7050-T76 Al Alloy

Material Flow Behavior and Thermal Cycle during Friction Stir Welding of AA5083/AZ91 Dissimilar Metals

Corrosion Behavior of Aluminum-Steel Weld-Brazing Joint

Microstructure and Mechanical Properties of Friction Stir-Welded Dissimilar Joints of ZK60 and Mg-4.6Al-1.2Sn-0.7Zn Alloys

Influence of Process Parameters on the Mechanical Properties and Corrosion Resistance of Dissimilar Friction Stir Welded Joints of AA2024-O and AA6061-O Aluminum Alloys

Mechanical properties and corrosion resistance study of dissimilar metal thin sheet friction stir welded joints

Electrochemical and mechanical behaviors of dissimilar friction stir welding between 5086 and 6061 aluminum alloy

Joining of Dissimilar Al and Mg Metal Alloys by Friction Stir Welding

Corrosion Behavior and Mechanical Properties of Al-Zn-Mg Aluminum Alloy Weld

Effect of Microstructure Evolution on Corrosion Behavior of 2195 Al-Li Alloy Friction Stir Welding Joint

Improved mechanical and corrosion properties of friction stir welded Al/Mg dissimilar lap joints by Zr interlayer addition

Microstructure and Mechanical Properties of Dissimilar Friction Stir Lap Welding Between AZ31 Mg Alloy and DC01 Steel