Improved ionic conductivity and Li dendrite suppression of PVDF-based solid electrolyte membrane by LLZO incorporation and mechanical reinforcement

Fei Chen,Mao-xiang Jing,Hua Yang,Wei-yong Yuan,Ming-quan Liu,Yong-sheng Ji,Shahid Hussain,Xiang-qian Shen

DOI: https://doi.org/10.1007/s11581-020-03891-0

IF: 2.961

2021-01-19

Ionics

Abstract:<p class="a-plus-plus">High room-temperature ionic conductivity and mechanical property are essential for the application of solid electrolyte. In this work, a poly(vinylidene fluoride) (PVDF)-based composite polymer solid electrolyte membrane (CSE) incorporated with Li<sub class="a-plus-plus">7</sub>La<sub class="a-plus-plus">3</sub>Zr<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">12</sub> (LLZO) fillers and high-strength porous skeleton was prepared. The introduction of LLZO increased the ionic conductivity of PVDF at room temperature by reducing the crystallinity of PVDF matrix, and the addition of skeleton greatly improved the mechanical property of electrolyte membrane and inhibited the growth of lithium dendrites. The prepared PVDF-LLZO CSE has a room-temperature ionic conductivity of 1.75 × 10<sup class="a-plus-plus">−4</sup> S/cm, and the tensile strength reaches 95 MPa, which greatly enhanced the ability of lithium dendrite suppression. The assembled LiNi<sub class="a-plus-plus">0.6</sub>Co<sub class="a-plus-plus">0.2</sub>Mn<sub class="a-plus-plus">0.2</sub>O<sub class="a-plus-plus">2</sub> (NCM622)/CSE/Li cell shows an initial capacity of 151 mAh/g with a retention capacity of 108 mAh/g after 100 cycles at the current density of 0.5 C. This ultrathin PVDF/LLZO CSE has a great application prospect in solid-state lithium batteries.</p>

chemistry, physical,physics, condensed matter,electrochemistry