Preparation and microwave dielectric properties of BPO4 ceramics with ultra-low dielectric constant

Xuan Wang,Lei Li,Wen Bin Hong,Han Yan,Shu Ya Wu,Xiang Ming Chen

DOI: https://doi.org/10.1007/s10854-021-05381-z

2021-02-10

Abstract:BPO₄ ceramics with a cristobalite-like structure were prepared via solid-state sintering (SSS) and spark plasma sintering (SPS). Significant shrinkage and grain growth were observed with increasing the sintering temperature up to 1200 °C for SSS samples, while the highest relative density is only 74.6% because of the serious sublimation of BPO₄, and the microwave dielectric properties of <i>ε</i>_<i>r</i> = 3.38, <i>Qf</i> = 18,200 GHz and <i>τ</i>_<i>f</i> = −42.8 ppm/°C were achieved at 14.6 GHz for SSS samples sintered at 1000 °C for 3 h. A much higher relative density of 92.7% was obtained in SPS sample (1000 °C/10 min) with <i>ε</i>_<i>r</i> = 4.20, <i>Qf</i> = 4,000 GHz, and <i>τ</i>_<i>f</i> = −20.7 ppm/°C. The <i>Qf</i> value increases by a factor of 6.9 and 5.9 with increasing frequency from 4.6 GHz to 14.6 GHz for SSS and SPS samples, respectively, which implies that the <i>Qf</i> value is dominated by extrinsic factors and has a huge improvement space. The corrected dielectric constant by porosity is only 4.65, indicating that BPO₄ ceramic is a promising candidate as the microwave substrate material if the relative density and microstructure can be further improved.