MSO4 (M = Ca, Sr, Ba) Microwave Dielectric Ceramics with Low Dielectric Constant

Ying Qiang Jia,Wei Kun Luo,Lei Li,Shu Ya Wu,Xiang Ming Chen

DOI: https://doi.org/10.1111/jace.18862

IF: 4.186

2023-01-01

Journal of the American Ceramic Society

Abstract:MSO4 (M = Ca, Sr, Ba) ceramics with relative densities exceeding 96% were prepared by solid-state sintering at low sintering temperatures of 625-875 degrees C, and their structures and microwave dielectric properties at 10-19 GHz were characterized. MSO4 ceramics crystallized in orthorhombic symmetry with the space groups of Amma for CaSO4 and Pnma for SrSO4 and BaSO4. The optimal microwave dielectric properties were obtained with epsilon(r) = 5.85, Qf = 57 000 GHz, tau(f,W) = -98.8 ppm/degrees C for CaSO4, epsilon(r) = 10.95, Qf = 15 500 GHz, tau(f,W) = 101.6 ppm/degrees C for SrSO4, and epsilon(r) = 9.42, Qf = 38 200 GHz, tau(f,W) = -4.7 ppm/degrees C for BaSO4. The increased epsilon(r) and tau(f,W) while decreased Qf value in the order of CaSO4, BaSO4, and SrSO4 were attributed to the enhanced rattling effect of M2+. Besides, the temperature dependence of tau(f) was weak for CaSO4 and BaSO4, whereas much stronger for SrSO4. As most low-epsilon(r) microwave dielectric ceramics are of large negative tau(f), the near-zero tau(f) of BaSO4 and positive tau(f) of SrSO4 are rare, indicating they are potential candidates for millimeter-wave communication as a temperature-stable dielectric ceramic and a compensator for tuning negative tau(f) to near-zero, respectively.