Development of FeCoMnAl multi-principal element alloys and soft magnetic powder cores with excellent magnetic properties and high temperature magnetic stability
Liping Yang,Yaqiang Dong,Wei Gao,Xingjie Jia,Junyao Zhang,Yanqiu Li,Qiang Li,Qikui Man,Baogen Shen
DOI: https://doi.org/10.1016/j.matdes.2024.112787
IF: 9.417
2024-02-26
Materials & Design
Abstract:In order to develop a multi-principal element alloy with outstanding soft magnetic properties and high thermal stability, a Fe 35 Co 35 Mn 30−x Al x (x = 9, 12, 15, 18, 21, 24) alloy system was designed. The findings demonstrated that the optimal Al/Mn content ratio contributes to the formation of a BCC and B2 dual-phase structure, which leads to a significant increase in the saturation magnetic flux density ( B s ) and a considerable decrease in the coercivity of the alloy. The as-cast Fe 35 Co 35 Mn 15 Al 15 alloy with a co-lattice structure exhibits exceptional soft magnetic properties, with a resistivity of 324 μΩ·cm, a B s of 1.46 T and a H c of 167.2 A/m. Corresponding soft magnetic powder cores (SMPCs) were fabricated and the impact of heat treatment temperature on the properties of the SMPCs was examined. The SMPCs after annealing at 660 °C exhibits high stable permeability ( μ e ) of 48 up to 10 MHz, a low core loss ( P cv ) of 1208 mW/cm 3 (at 1 MHz, 20 mT), and excellent direct current bias performance. In addition, these SMPCs possess excellent high temperature magnetic stability, and the variation of both μ e and P cv at a high frequency (1 MHz) is less than 2 % over a wide temperature range of 25–150 °C.
materials science, multidisciplinary