Effects of Y and Addition of Refiners on Hot Tearing Susceptibility of MgZn-Based Alloy

Z. Q. Wei,Z. J. Zhou,S. M. Liu,Z. Liu,Y. Wang

DOI: https://doi.org/10.1007/s40962-021-00591-x

2021-04-12

International Journal of Metalcasting

Abstract:<p class="a-plus-plus"> On the basis of studying the effect of rare earth elements on hot tearing susceptibility (HTS) of Mg–Zn alloys, further exploring effective ways to reduce HTS of Mg–Zn–Y alloys are very important for the development and application of magnesium alloys. In this paper, the effects of 2 at% Y on HTS of MgZn<sub class="a-plus-plus">1</sub> alloy and several grain refiners on HTS of MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub> alloy were studied. The modified Clyne–Davies model is used to predict the HTS of the investigated alloys, which are found in the descending order: MgZn<sub class="a-plus-plus">1</sub> &gt; MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub> &gt; MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub>–0.5 wt% Na<sub class="a-plus-plus">2</sub>CO<sub class="a-plus-plus">3</sub> &gt; MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub>–0.5 wt% Ti &gt; MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub>–0.5 wt% Zr. By means of XRD, SEM, TEM and EBSD, the evolution of the microstructure during solidification is revealed. The results show that the addition of 2 at% Y can not refine α-Mg grains, but it can change the precipitation type of the second phase. When the precipitation type of the second phase changes from Mg<sub class="a-plus-plus">7</sub>Zn<sub class="a-plus-plus">3</sub> to Mg<sub class="a-plus-plus">12</sub>ZnY (LPSO phase) and Mg<sub class="a-plus-plus">3</sub>Zn<sub class="a-plus-plus">3</sub>Y<sub class="a-plus-plus">2</sub> (W-phase), the solidification end temperature of the alloy increases by more than 100 °C, and the coherent lattice of LPSO and α-Mg has a better bridging effect on the grain boundary, which reduces the HTS by 28.4%. Moreover, the addition of 0.5 wt% Na<sub class="a-plus-plus">2</sub>CO<sub class="a-plus-plus">3</sub>, 0.5 wt% Ti or 0.5 wt% Zr is an effective method for α-Mg grain refinement, equiaxation and dendrite coherent delay of MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub> alloy. In particular, the addition of 0.5 wt% Zr can reduce the α-Mg grain size of MgZn<sub class="a-plus-plus">1</sub>Y<sub class="a-plus-plus">2</sub> alloy by 89.1% and increase the solid fraction by 45% when dendrites are coherent, which results in a 77.1% reduction in HTS.</p>

metallurgy & metallurgical engineering