Q-switching and mode-locking pulse generation in Ytterbium-doped fiber lasers using nanomaterial saturable absorbers / Ahmed Hasan Hamood al-Masoodi
Hamood al-Masoodi,A. Hasan
Abstract:This research work focuses on exploring various new nanomaterials for saturable
absorber (SA) application in generating Q-switched and Mode-locked pulses operating at
1 μm region. These nanomaterials are Molybdenum disulfide (MoS2), Black Phosphorus
(BP), Topological Insulator (TI): Bismuth (III) Selenide (Bi2Se3), Bismuth (III) Telluride
(Bi2Te3), and antimony telluride (Sb2Te3), and metal oxide: Nickle Oxide (NiO)
nanoparticles and cobalt oxide (Co3O4) nanocubes. The fiber laser employs Ytterbiumdoped
fiber (YDF) as a gain medium. Firstly, molybdenum disulfide (MoS2) was
proposed. The Q-switched laser was obtained by using few layers MoS2, which was
mechanically exfoliated by using a scotch tape. The SA was sandwiched between two
fiber ferrules to form a fiber compatible Q-switcher. By incorporating the SA inside the
YDFL cavity, a stable pulse laser operating at 1070.2 nm wavelength was generated with
the repetition rate was tunable from 3.817 to 25.25 kHz. A passively mode-locked YDFL
was demonstrated using a few layered MoS2 film which was obtained by a liquid phase
exfoliation technique. The mode-locking pulses have a repetition rate of 18.8 MHz and
pulse energy of 0.1 nJ. Secondly, mechanically exfoliated Black phosphorus (BP) was
proposed for both Q-switching and mode-locking pulses generation. The Q-switched
laser has a pump threshold of 55.1 mW, a pulse repetition rate that is tunable from 8.2 to
32.9 kHz, the narrowest pulse width of 10.8 μs and the highest pulse energy of 328 nJ.
BP based mode-locked YDFL was obtained by improving the SA preparation. The laser
operated at 1033.76 nm with a fixed repetition rate of 10 MHz. Passively Q-switched
YDFLs was also successfully demonstrated using a few-layers Bi2Se3, Bi2Te3 and antimony telluride (Sb2Te3) based SAs. For instance, a Sb2Te3 film based Q-switched
YDFL produced pulse repetition rate, which was tunable from 24.4 to 55 kHz with the
maximum pulse energy of 252.6 nJ at 82.3 mW pump power. The mode-locked YDFL
operating at 24.2 MHz repetition and 18.8 ps pulse width were also realized with Sb2Te3
based SA. Finally, two transition metal oxide nanomaterials: Nickel Oxide (NiO) and
cobalt oxide (Co3O4) were embedded into a polymer film, making it an SA device for
both Q-switched and mode-locked YDFLs. Stable Q-switched and mode-locked YDFLs
were realized with both materials. For instance, the mode-locked Co3O4 based YDFL was
operated at 1035.8 nm wavelength with a fixed repetition rate of 20 MHz and picoseconds
pulse width. In short, an efficient and low-cost Q-switched and mode-locked YDFLs
operating in 1 μm region have been successfully achieved by utilizing various new
nanomaterials as SA.
Materials Science,Engineering,Physics