Abstract:We investigate the rf performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120–165 °C for an extended period of time (24–48 h) either in high vacuum or in a low partial pressure of ultrapure nitrogen. The improvement in Q0 with a Q rise was observed when nitrogen gas was injected at ∼300 °C during the cavity cooldown from 800 °C and held at 165 °C , without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing rf field, resulting in a Q rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of ∼0.95 GHz above that the Q rise phenomenon occurs at 2 K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance. https://doi.org/10.1103/PhysRevAccelBeams.27.062001 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Published by the American Physical Society

Niobium and niobium-titanium nitrides for RF applications

Advancement in the understanding of the field and frequency dependent microwave surface resistance of niobium

Metallurgical and Technological Request for High Purity Niobium in SRF Application

Nitrogen and argon doping of niobium for superconducting radio frequency cavities: a pathway to highly efficient accelerating structures

On the quest of low temperature nitrogen infusion relevant for superconducting Nb based radio-frequency cavities

Investigation into surface composition of nitrogen-doped niobium for superconducting RF cavities

Field, frequency and temperature dependence of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Temperature-dependent near-surface interstitial segregation in niobium

Fabrication and Radio Frequency Test of Large-Area MgB2 Films on Niobium Substrates

Systematic study of niobium thermal treatments for superconducting radio frequency cavities employing X-ray photoelectron spectroscopy

Field, frequency, and temperature dependencies of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

In-situ Synchrotron X-Ray Photoelectron Spectroscopy Study of Medium-Temperature Baking of Niobium for SRF Application

Muon spin rotation studies of niobium for superconducting rf applications

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Enhancement in Quality Factor of SRF Niobium Cavities by Material Diffusion

Unprecedented Quality Factors at Accelerating Gradients up to 45 MV/m in Niobium Superconducting Resonators via Low Temperature Nitrogen Infusion

Atomic Layer Deposition Niobium Nitride Films for High-Q Resonators

The Rise of Ingot Niobium as a Material for Superconducting Radiofrequency Accelerating Cavities

ZrNb(CO) RF superconducting thin film with high critical temperature in the theoretical limit

Demonstration of Niobium Tin in 218 MHz Low-beta Quarter Wave Accelerator Cavity

Growth and Characterization of a Kind of Nitrogen-Rich Niobium Nitride for Bolometer Applications at Terahertz Frequencies