Abstract:As a result of a collaboration between Jefferson Lab and niobium manufacturer CBMM, ingot niobium was explored as a possible material for superconducting radiofrequency (SRF) cavity fabrication. The first single cell cavity from large grain high purity niobium was fabricated and successfully tested at Jefferson Lab in 2004. This pioneering work triggered research activities in other SRF laboratories around the world. Large grain niobium became not only an interesting alternative material for cavity builders, but also material scientists and surface scientists were eager to participate in the development of this material. Most of the original expectations for this material of being less costly and allowing less expensive fabrication and treatment procedures at the same performance levels in cavities have been met. Many single cell cavities made from material of different suppliers have been tested successfully and several multi-cell cavities have shown the performances comparable to the best cavities made from standard poly-crystalline niobium. Several 9-cell cavities fabricated by Research Instruments and tested at DESY exceeded the best performing fine grain cavities with a record accelerating gradient of Eacc = 45.6 MV/m. Recently- at JLab- by using a new furnace treatment procedure a single cell cavity made of ingot niobium performed at a remarkably high Q0-value (~5x10^10) at an accelerating gradient of ~20 MV/m, at 2K. Such performance levels push the state-of-the art of SRF technology to new limits and are of great interest for future accelerators. This contribution reviews the development of ingot niobium technology and attempts to make a case for this material being the choice for future accelerators.

Fabrication and Radio Frequency Test of Large-Area MgB2 Films on Niobium Substrates

MgB2films Fabricated on Molybdenum Substrate by Hybrid Physical–chemical Vapor Deposition for Superconducting RF Cavity Applications

MgB$_{2}$ Coating by HPCVD for 1.3-GHz Superconducting RF Cavities

Wafer-Scale MgB2 Superconducting Devices

High Quality MgB2/Nb Deposited by HPCVD Method

MgB2 Thick Films on Three-Dimensional Structures Fabricated by HPCVD

Film Fabrication and Electronic Devices of MgB2 Superconductor

Fabrication of Superconducting Nanowires from Ultrathin MgB2 Films Via Focused Ion Beam Milling

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

The Rise of Ingot Niobium as a Material for Superconducting Radiofrequency Accelerating Cavities

Medium grain niobium SRF cavity production technology for science frontiers and accelerator applications

Superconducting DC and RF Properties of Ingot Niobium

Study of Micron-Thick Mgb2 Films on Niobium Substrates

Enhanced radio-frequency performance of niobium films on copper substrates deposited by high power impulse magnetron sputtering

Thickness effect on superconducting properties of niobium films for radio-frequency cavity applications

Fabrication of superconducting magnesium diboride thin films by electron beam annealing

Effective medium temperature baking of 1.3 GHz single cell SRF cavities

MgB2 Films on Nb Substrate and Its Bending Test

Mechanical and superconducting properties of kilometer level,Nb reinforced,6+1 filamentary MgB_2wires

Investigation of Nb–B Diffusion and the Superconducting Properties of MgB2/Nb/Cu Tapes