Abstract:Titanium alloys can achieve ultrahigh strength through precipitation hardening of secondary alpha-phase (alpha s) from ,B-matrix but often compromise ductility due to the conventional strength-ductility trade-off. In this study, a new strategy based on ,B-subgrains-mediated hierarchical alpha-precipitation is devised to balance the conflict in Ti-6Al-2Mo-4Cr-2Fe (wt.%) alloy through a unique combination of hot rolling, short-term solid solution, and aging treatment, i.e., RSST + A. Tensile testing reveals that the RSST + A samples exhibit ultrahigh strength of similar to 1581 MPa and decent ductility of similar to 8.4 %, surpassing similar to 1060 MPa and similar to 2.7 % of the corresponding RSST counterparts without final aging treatment. This remarkable strengthening and counterintuitive ductilizing is attributed to the architecting of ,B-subgrains-mediated hierarchical alpha- precipitates as a result of our specific processing approach. The designed short-term solution introduces abundant ,B subgrains that are transformed from the retained intensive dislocations during hot rolling. The ,B subgrain boundaries subsequently promote a dramatic precipitation of alpha allotriomorphs (alpha GB) and Widmanst & auml;tten side-plates (alpha WGB), which effectively subdivides ,B grains into numerous tiny independent deformation units. Consequently, plastic strain is uniformly partitioned into a large number of small aged ,B subgrains during tension, which strongly impedes strain localization that would typically occur across multiple ,B subgrains in the fashion of long straight slip bands in the case of the RSST samples. Furthermore, the hierarchical alpha structure also postpones uncontrollable cracking even when structural damage occurs at the last stage of straining. These findings demonstrate that appropriately manipulating microstructure through elaborately designing processing routes enables unexpectedly ductilizing high- strength titanium alloys in the precipitation-hardening state. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Synthesis of New Metastable Aluminum-Titanium Alloy by Defying Equilibrium in an Equilibrium Process

Metastable Beta Titanium Alloys: Tuning the Beta Phase Stability and Low-Temperature Martensitic Transformation of Metastable Beta Titanium Alloys

Recent Advances in the Design of Novel Β‐titanium Alloys Using Integrated Theory, Computer Simulation, and Advanced Characterization

Design of Metastable Β-Ti Alloys with Enhanced Mechanical Properties by Coupling Αs Precipitation Strengthening and TRIP Effect

Achieving High Strength and Ductility of a Metastable Β-Titanium Alloy Via Coupling Thermomechanical Processing and Heat Treatments

Spinodal Decomposition-Mediated Multi-Architectured Α Precipitates Making a Metastable Β-Ti Alloy Ultra-Strong and Ductile

Alloying Design of Titanium Aluminum Intermetallics and Research Progress

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Fabrication of Highly Heterogeneous Precipitate Microstructure in an Α/β Titanium Alloy

Exploration of Nano-scale Structural Instabilities in Metastable Β Titanium Alloys Using Advanced Electron Microscopy

Surface Modification and Alloying of Aluminum and Titanium Alloys with Low-Energy, High-Current Electron Beams

Phase relationships and transformations in the ternary aluminum—titanium—tantalum system

Making Titanium Alloys Ultrahigh Strength and Toughness Synergy Through Deformation Kinks-Mediated Hierarchical Α-Precipitation

Mechanical alloying and thermal analysis of Ta–Ti alloys

Research Progress on Composition Design, Deformation Mechanism and Mechanical Properties of Metastable Titanium Alloy

Design a Strong and Ductile Novel Metastable Β-Ti Alloy with Multi-Scale Α Precipitates Utilizing Spinodal Decomposition

Exploration of Novel Nano-scale Instabilities in Metastable Beta Titanium Alloys Using Transmission Electron Microscopy and Aberration-Corrected Scanning Transmission Electron Microscopy

Examination of Novel Titanium-639 Alloy as a Means of Balancing Strength and Ductility through Molybdenum Addition Rather than Prolonged Aging Heat Treatment

Enhancing Strength-Ductility Synergy in Metastable Β-Ti Alloys Through Β-Subgrains-mediated Hierarchical Α-Precipitation

Oxygen interstitials make metastable β titanium alloys strong and ductile

Behaviour of novel low-cost blended elemental Ti-5Fe-xAl alloys fabricated via powder metallurgy