Abstract:Nanostructured niobium-titanium carbonitrides, (Nb,Ti)C1-xNx, with the cubic-rock salt structure are prepared without the use of reactive gases via thermal treatment (700-1200 °C) under nitrogen of mixtures of guanidine carbonate and ammonium niobate (V) oxalate hydrate, with addition of ammonium titanyl oxalate monohydrate as a titanium source. The bulk structure and chemical composition of the materials are characterized using powder X-ray diffraction (XRD) and powder neutron diffraction, elemental homogeneity is studied using energy dispersive spectroscopy (EDS) mapping using transmission electron microscopy (TEM), and surface chemical analysis is examined using X-ray photoelectron spectroscopy (XPS). Nanoscale crystallites of between 10 and 50 nm are observed by TEM, where EDS reveals the homogeneity of metal distribution for the mixed-metal materials. Titanium carbonitrides are found to be air sensitive, reacting with air under ambient conditions, while titanium-niobium carbonitrides are found to degrade in aqueous sulfuric acid. The niobium carbonitrides, however, show some stability toward acidic solutions. Materials are produced with composition NbC1-xNx with x between 0.35 and 0.45, and more carbon-rich materials (x ≈ 0.35) are found as the synthesis temperature is increased, as proven by Rietveld refinement of crystal structure against powder neutron diffraction data. Despite phase purity seen by diffraction and negligible bulk carbon content, XPS shows a complex surface chemistry for the NbC1-xNx materials, with evidence for Nb2O5-like oxide species in a carbon-rich environment. The NbC1-xNx prepared at 900 °C has a surface area around 50 m2 g-1, making it suitable as a catalyst support. Loading with iridium provides a material active for the oxygen evolution reaction in 0.1 M sulfuric acid, with minimal leaching of either Nb or Ir after 1000 cycles.

Selective, low-temperature synthesis of niobium carbide and a mixed (niobium/tungsten) carbide from metal oxide-polyacrylonitrile composites by carbothermal reduction

Synthesis and Oxidation Behavior of Nanocrystalline Niobium Carbide

Controlled Synthesis of Niobium and Rare Earth Mixed Oxides for Catalytic Combustion of Chlorinated Vocs in the Synthesis Process of Polyether Polyol and Polyurethane

Synthesis of niobium(iv) carbide nanoparticles via an alkali-molten-method at a spatially-limited surface of mesoporous carbon

Synthesis mechanism and electrical conductivity of NbC O1- solid solution

Synthesis of Niobium Carbonitride by Thermal Decomposition of Guanidine Oxaloniobate and Its Application to the Hydrodesulfurization of Dibenzothiophene

New insights into the formation mechanism of the multicomponent carbides (Nb, M)C (M = Ti, Cr and Mn)

Nanostructured Niobium and Titanium Carbonitrides as Electrocatalyst Supports

Synthesis and Characterization of Superconducting NbC Nanotubes

A Tungsten-Based Nanolaminated Ternary Carbide: (W,Ti)4C4- x

Preparation of high-entropy (Ti,Nb,Ta,Mo,W)(C,N) ceramics via carbothermal reduction nitridation using different carbon source

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Low‐temperature synthesis and oxidation resistance of random combination of Hf, Nb, and Ta carbides microcuboids

Synthesis of nano (Ti,W)C powder with preferred orientation and twin boundary structure

Microstructure and wear properties of niobium carbide particulates gradient-distribution composite layer fabricated in situ

Effect of Doped Niobium on the Microstructure and Properties of W–Nb/TiC Composites Prepared by Spark Plasma Sintering

Direct production of the Nb-10%W-l%Zr-0.1%C alloys from the constituent metal oxides by the combined carbothermal reduction-electron beam melting method

Synthesis of Nanostructured Tungsten Carbide (WC) from Ammonia Paratungstate-APT and its Characterization by XRD and Rietveld Refinement

Kinetic mechanism in the process of carbothermal reduction of ferrum niobate

Ordered Mesoporous Nanocrystalline Titanium‐Carbide/Carbon Composites from in Situ Carbothermal Reduction

Crystallization characteristics and chemical bonding properties of nickel carbide thin film nanocomposites