Abstract:Nanocrystalline Ni-Mo alloy coatings with excellent brightness, high hardness, and corrosion resistance were prepared. Nanocrystalline Ni-Mo alloy coating with a Mo content of 14.94 at% was electrodeposited on the copper foil substrate under the optimized conditions with the current efficiency of 51.64%. The electrodeposition behavior of Ni-Mo alloy coatings was studied by cathodic polarization curve and chronopotentiometry. Chronopotentiometry showed that the nucleation rate of Ni-Mo alloys can be accelerated with the increase of current density. Meanwhile, the cathodic polarization curves show that the additives can effectively inhibit the electrodeposition of Ni-Mo alloys. The (2 0 0) and (2 2 0) diffraction peaks of Ni gradually disappeared and the grain size gradually decreased with the increase of Mo content in the alloy coating according to XRD and TEM analysis. Scanning electron microscope (SEM) and confocal microscope observation results show that the coating becomes smoother and denser with the increase of Mo content when Mo content was lower than 14.94 at%, after which the density of the coating saw a decline due to the intensified hydrogen evolution reaction. The microhardness results of the alloy coating show that the microhardness of the alloy coating is related to the solid solution strengthening, texture evolution, and plastic deformation of the alloy. Meanwhile, the alloy coating has a Hall-Petch relationship and inverse Hall-Petch relationship, and the critical grain size is 5.5 nm. The corrosion resistance of Ni-Mo alloy coating is better than that of pure Ni coating, and the corrosion resistance is optimal when the Mo content is about 15 at%. In addition, in the plating solution containing additives, the deposited Ni-Mo alloy coating is smoother and denser, and the hardness and corrosion resistance of the alloy coating is also greatly improved.

A Study of Molybdenum Coatings Underpotential Preparation in an Ionic Liquid System

Electrodeposition of Molybdenum in the [BMP]Tf2N Ionic Liquid at Low Temperature

Electrodeposition of Molybdenum from Water-in-Acetate Electrolytes

Electrodeposition of nanocrystalline Ni-Mo alloys in pyrophosphate baths

Electrodeposition of Ni–Mo alloy coatings from choline chloride and propylene glycol deep eutectic solvent plating bath

Preparation of Electrochemical Ni–Mo Coatings from Self-Regulating Electrolytes

Electrodeposition of Nanocrystalline Chromium Coatings from 1-Butyl-3-methylimidazolium-hydrogen Sulfate Ionic Liquid

Electrodeposited MoxSyOz/Ni Tribological Coatings

Electrodeposition and Corrosion Analysis of Ni-Mo Alloy Coatings

Fabrication and Characterization of Oxygen-Carbon-Contained CrMnFeCoNi Coatings Electrodeposited in DMF-CH3CN Solution with and Without Supporting Electrolyte LiClO4

Electrochemical behavior and cathodic nucleation mechanism of molybdenum ions in NaCl-KCl

Influence of Mo addition on the structural and electrochemical performance of Ni-rich cathode material for lithium-ion batteries

Amorphous Al–Mn Coating on NdFeB Magnets: Electrodeposition from AlCl3–EMIC–MnCl2 Ionic Liquid and Its Corrosion Behavior

Electrochemical Behavior of Cobalt from 1-Butyl-3-methylimidazolium Tetrafluoroborate Ionic Liquid

Electrochemical Synthesis and Characterization of Ni–P Alloy Coatings from Eutectic–Based Ionic Liquid

Preparation of electrodeposited Mo-Ni coating and its spectral properties

Molybdenum Deposition on the Thin Alumina Film: A Combinatorial Investigation by HREELS, XPS and UPS

Electrodeposition of Molybdenum Disulfide (MoS2) Nanoparticles on Monocrystalline Silicon

Electroless Ni–P plating with molybdate pretreatment on Mg–8Li alloy

Liquid zinc assisted electro-extraction of molybdenum

Electrodeposition of High-Quality Cr Coatings with Solid Solution Al from Cr2+ Electrolyte