Investigation on the Tribological Behaviors of As-Sprayed Al2O3 Coatings Sealed with MoS2 Dry Film Lubricant

Wen Deng,Lin Tang,Hui Qi,Changfu Zhang

DOI: https://doi.org/10.1007/s11666-021-01218-7

IF: 2.839

2021-06-09

Journal of Thermal Spray Technology

Abstract:The Al₂O₃-MoS₂ ceramic-based lubricating coating was prepared via introducing MoS₂ dry film lubricant into the micro-defects of thermally sprayed Al₂O₃ coating by paint spraying method. The microstructure, mechanical properties and tribological behaviors of the as-received Al₂O₃-MoS₂ coating are thoroughly evaluated. The results illustrated that MoS₂ was mainly concentrated on the shallow surface of the Al₂O₃ coating, and thus more compact and smoother Al₂O₃-MoS₂ coating was obtained. Meanwhile, the mechanical properties of the Al₂O₃ coating did not change significantly after the introduction of MoS₂. The tribological experiments illustrated that compared with the Al₂O₃ coating, the friction coefficient and specific wear rate of the Al₂O₃-MoS₂ coating under different loads were greatly reduced due to the generation of the lubricating layer. Especially under the load of 5 N, the friction coefficient was as low as 0.36, and the wear rate (1.49 × 10⁻⁵ mm³ (N m)⁻¹) was about one order of magnitude lower than that of Al₂O₃ coating (2.53 × 10⁻⁴ mm³ (N m)⁻¹). This research established a new and simple way to prepare ceramic-based self-lubricating coatings by using temperature-sensitive solid lubricants.

materials science, coatings & films