Superhydrophobic MoS 2 Nanosheet–Cu 2 O Nanoparticle Antiwear Coatings
Chunmeng Dong,Dong Jiang,Yanlong Fu,Desheng Wang,Qinqin Wang,Lijun Weng,Ming Hu,Xiaoming Gao,Jiayi Sun
DOI: https://doi.org/10.1021/acsanm.1c00842
IF: 6.14
2021-04-28
ACS Applied Nano Materials
Abstract:The superhydrophobic MoS<sub>2</sub> nanosheet–Cu<sub>2</sub>O nanoparticle antiwear coatings were constructed by immersing the sputtered MoS<sub>2</sub> coatings to a solution of CuSO<sub>4</sub> and sodium citrate. The contact angle (CA) and sliding angle (SA) of the coatings were ∼164 and 2°, respectively. MoS<sub>2</sub> nanosheets wrapped with Cu<sub>2</sub>O layers were ∼54 nm thick. On the nanosheets, the Cu<sub>2</sub>O nanospheres were ∼60 nm in size, and numerous Cu<sub>2</sub>O nanospheres aggregated into Cu<sub>2</sub>O clusters with 1–5 μm length. The cooperation of microstructures (Cu<sub>2</sub>O clusters) and nanostructures (Cu<sub>2</sub>O nanoparticles) and the arrangement of the Cu<sub>2</sub>O clusters on the surface of the sputtered MoS<sub>2</sub> coatings resulted in the superhydrophobic property of the MoS<sub>2</sub> nanosheet–Cu<sub>2</sub>O nanoparticle coating. Besides, the MoS<sub>2</sub> nanosheet–Cu<sub>2</sub>O nanoparticle coating showed outstanding stability and durability (almost 1 year) with superhydrophobic and tribological properties, including a relatively low friction coefficient (as low as 0.008–0.015) and a long antiwear life (∼1.0 × 10<sup>6</sup> r). During friction, Cu<sub>2</sub>O nanospheres can roll at the friction interface, show "nanobearing effects", and then reduce the friction coefficient of the coatings.This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology