Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

(Y, Gd)H2 phase formation in as-cast Mg-6Gd-3Y-0.5Zr alloy

Microstructure of as-cast Mg-4.2Zn-0.8Y (at.%) alloys containing Gd

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and mechanical properties of cast Mg-6Gd–Zr alloy with different Y addition

Unveiling precipitation behavior in Mg-Y based alloys

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Microstructure and Precipitates in Mg-Zn-Y Alloys

Characterization of β precipitate phase in Mg-7Gd-5Y-1Nd-0.5Zr alloy

Morphology and crystallography of β precipitate phase in Mg-Gd-Y-Nd-Zr alloy

Study on phase constitutions, growth pattern and mechanical properties of Mg-1.4Gd-1.2Y-xZn-0.15Zr (at%) alloys

Disclosing Differential Precipitation Behavior of a Novel High Mg-containing Al-Mg-Zn-Si Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Crystal structure, phase content, and tensile properties of As-cast Mg–Gd–Y–Al alloys

Tuning texture and precipitation using Y/Gd atomic ratio in iso-concentration Mg–Y–Gd–Ag–Zr extruded alloys

A kind of sandwich-combined precipitate formed in a duplex-aged Mg-Gd-Y alloy

Effect of Gd content on microstructure and dynamic mechanical properties of solution-treated Mg−xGd−3Y−0.5Zr alloy