Preparation of the First Electrolytic Plutonium and of Uranium from Fused Chlorides

M. Kolodney

DOI: https://doi.org/10.1149/1.2123562

IF: 3.9

1982-11-01

Journal of The Electrochemical Society

Abstract:The production at Los Alamos of the first electrolytic plutonium is described. Because it was scarce, it was initially prepared on a 50 mg scale. The electrolyte consisted of PuCl3 dissolved in a ternary eutectic of BaCl2‐KCl‐NaCl and was operated at 660°C. The technique involved the electrolysis of as little as 0.1 cm3 of fused salt in a glass cell to produce liquid metal. Subsequently, a few successful 1g electrolyses were carried out with a maximum recovery of 75% of the plutonium content of the bath. It was found that the plutonium trichloride had to be dry and relatively low in oxygen and was, therefore, best prepared by dry methods. Electrolyses were performed under purified argon or hydrogen using tungsten or graphite anodes. The metallic product was pure and was used for early development of methods for cleaning, etching, and plating plutonium. Uranium was used for finding and testing techniques before plutonium became available. Acceptable deposits could not be obtained from UCl4 dissolved in the ternary chloride eutectic, but were produced when UCl3 was substituted for the tetrachloride. At about 650°C, the uranium was deposited in the form of solid, dendritic crystals. These were, in general purer than the starting materials and were readily converted to massive metal.

electrochemistry,materials science, coatings & films