Large-scale manufacturing route to metamaterial coatings using thermal spray techniques and their response to solar radiation

Nadimul Haque Faisal,Nazmi Sellami,Federico Venturi,Tanvir Hussain,Tapas Mallick,Firdaus Muhammad-Sukki,Alex Bishop,Hari Upadhyaya,Nirmal Kumar Katiyar,Saurav Goel

DOI: https://doi.org/10.1007/s42247-021-00252-z

2021-07-04

Emergent Materials

Abstract:Abstract Metamaterials, an artificial periodic two- or three-dimensional configuration, can change propagation characteristics of electromagnetic waves (i.e., reflection, transmission, absorption). The current challenges in the field of metamaterial coatings are their manufacturing in a large-scale and large-length scale. There is a clear need to enhance process technologies and scalability of these. Thermal spraying is a method used to deposit small- to large-scale coatings where the sprayed layer is typically formed by the successive impact of fully or partially molten particles of a material exposed to various process conditions. This work aims to investigate the feasibility to manufacture large scale metamaterial coatings using the thermal spray technique and examine their response to solar radiation. Two types of coatings namely, Cr 2 O 3 and TiO 2 , were deposited onto various substrates (e.g., steel, aluminium, glass, indium tin oxide (ITO)–coated glass) with a fine wire mesh (143 μm and 1 mm aperture sizes) as the masking sheet to manipulate the surface pattern using suspension high-velocity oxy-fuel thermal spraying (S-HVOF) and atmospheric plasma-sprayed (APS) methods, respectively. Post deposition, their responses subjected to electromagnetic wave (between 250 and 2500 nm or ultraviolet (UV)-visible (Vis)-infrared (IR) region) were characterised. The additional microstructural characterisation was performed using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), three-dimensional profilometry, and optical spectroscopy. It is demonstrated that through novel application of thermal spray techniques, large-scale manufacturing of metamaterial coating is possible, and such material can affect electromagnetic wave propagation. Comparison between Cr 2 O 3 and TiO 2 coatings on aluminium substrates showed reduced three orders of reduced reflectance for Cr 2 O 3 coatings (for 1-mm aperture size) throughout the spectrum. It was concluded that for a similar bandgap, Cr 2 O 3 coatings on aluminium substrate will yield improved optical performance than TiO 2 coating, and hence more useful to fabricate opto-electronic devices. Graphical abstract