Physical, Mechanical, and Tribological Properties of Industrial Waste Fly Ash Reinforced AA5083 Composites Fabricated by Stir Casting Process

Swati Gangwar,Ranjeet Kumar Singh,Prabhat Chand Yadav,Sandeep Sahu

DOI: https://doi.org/10.1007/s40735-021-00560-1

2021-07-09

Abstract:Reinforcement of second phase particle in metal/alloy to develop metal matrix composite is a standard practice to enhance various properties required for commercial applications. In this work, an industrial waste, fly ash, has been used as reinforcement in aluminum alloy AA5083 to improve its physical, mechanical, and tribological properties. The metal matrix composites were fabricated using high temperature vacuum stir casting technique with varying fraction of fly ash (viz. 0, 4, and 8 wt.%). Reinforcement of fly ash in Al alloy improved its hardness from ~ 50 BHN (for initial alloy) to ~ 70 BHN for 8 wt.% fly ash. Meanwhile, impact strength indicated a reverse trend in comparison to that of hardness, with a marginal change in values from 258 to 248 J. Wear behavior of fabricated composites was investigated against EN31 hardened steel disc at different process parameters, viz. fly ash content, sliding velocity, and normal load. Worn surface of samples were examined under scanning electron microscope to find the wear mechanism. It showed severe abrasive grooves along with brittle fracture for lower fraction of fly ash (i.e., 0 and 4 wt.%), while mild abrasion followed by fragmentation of protective tribolayer was observed for the larger fraction of fly ash (i.e., 8 wt.%). The optimum condition among various process parameters for minimum sliding wear was obtained by Taguchi design of experiments. The minimum wear rate was obtained for 8 wt.% fly ash reinforced composite at sliding velocity 1.047 m/s and normal load 15 N.