Abstract:Fast growing poplar wood poses significant challenges including low mechanical strength, poor dimensional stability and weak texture, limiting its direct application in the field of building structures and decoration. We treated poplar wood using compression, digital printing and waterproofing techniques to develop a green structure-decoration integrated material. The compression treatment significantly improved the wood density, fiber orientation and surface smoothness. At a compression ratio of 60 %, poplar veneer demonstrates remarkable improvements in modulus of elasticity (MOE), modulus of rupture (MOR) and surface smoothness, with increases of 222.53 %, 233.53 % and 93.20 %, respectively, compared to uncompressed wood. Notably, this compression treatment reduces the surface roughness of poplar to 0.75 μm, meeting the flatness requirements for digital printing. Consequently, clear textures and vibrant colors are directly printed onto the flat surface of compression-densified poplar wood, eliminating the need for traditional surface sanding pre-treatment process, and accordingly improving the efficiency of the material preparation. Furthermore, a final waterproofing emulsion spraying treatment creates a dense micro/nanoscale hierarchical structure on the surface, enabling the compression-densified poplar wood samples to achieve MOE and MOR of 14.15 GPa and 123.00 MPa respectively, even after water absorption and re-dried processes. These values consistently exceed the standard value of MOE (12.50 GPa) and MOR (35.00 MPa) for the highest grade (TCT40) specified in GB50005-2017, indicating significantly improved structural stability. The structure-decoration integrated materials developed in this study offer high strength and dimensional stability, making them promising candidates for high value utilization in prefabricated wooden buildings.

Temperature’s effect on color change and mechanical properties of poplar powder compact formed by warm compaction

Effect of temperature on color and chemical composition of poplar powder compacts during warm-press forming

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

The relationship between color and mechanical properties of heat-treated wood predicted based on support vector machines model

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Dyeing of Poplar Wood Through High-Pressure Processing: Performance Evaluation

Mechanical Properties and Dimensional Stability of Poplar Wood Modified by Pre-Compression and Post-Vacuum-Thermo Treatments

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

Plastic and Elastic Strains in Poplar Wood under High-Pressure Densification

Integrated approach for improving mechanical and high-temperature properties of fast-growing poplar wood using lignin-controlled treatment combined with densification

Densification of poplar veneer

Effects of High-Temperature Heat Treatment Modification by Impregnation on Physical and Mechanical Properties of Poplar

Microstructure and chemical composition of compressed and carbonized poplar

Study on Poplar Densification by Cross-Grain Compression

Mechanical properties of industrial heat-treated wood

Effect of thermal treatment with water, H2SO4 and NaOH aqueous solution on color, cell wall and chemical structure of poplar wood

Preparation Optimization of Enhanced Poplar Wood by Organic–Inorganic Hybrid Treatment via Response Surface Methodology

Intenzitet toplinske modifikacije topolovine. Dio 2

Developing poplar wood into a green structure-decoration integrated material for prefabricated wooden building application

Effect of superheated steam pressure on the physical and mechanical properties of sandwich-densified wood

Response relationships between the color parameters and chemical compositions of heat-treated wood