Abstract:Phenolic resin-modified materials partially reduce the toughness of the wood. In this study, organic–inorganic composite modifiers were used to modify the wood. Silica sol/phenolic resin was prepared through in-situ polymerization, and poplar wood was modified using a vacuum pressure impregnation process, enhancing its toughness. Orthogonal experiments were conducted, and the impact toughness of the modified poplar wood was used as the evaluation index. Through orthogonal experiments, using the impact toughness of modified poplar as the evaluation indicator, it was found that when the average particle size of the silica sol is 8–15 nm, the pressure is 1.2 MPa, and the pressurization time is 3 h, the impregnation-modified poplar's impact toughness reaches its optimum, improving by 84.1% and 135.4% compared to the raw material and phenolic resin impregnated wood, respectively. The Fourier Transform Infrared Spectroscopy (FT-IR) results indicated that the characteristic absorption peak of Si-O-Si appears in the poplar wood after impregnation, confirming the formation of new silicon-oxygen (Si-O) chemical bonds. X-ray Photoelectron Spectroscopy (XPS) analysis revealed that a chemical reaction occurs between the impregnation liquid and the wood, generating Si-O-C. Subsequently, through Dynamic Mechanical Analysis (DMA) and Thermogravimetric (TGA) analysis, it was understood that this chemical reaction significantly enhances the thermal stability and toughness of the impregnated material, making it superior to the original poplar material. The TGA further unveiled that, compared to untreated poplar, the thermal stability of the impregnated material has been notably improved. Lastly, Scanning Electron Microscopy (SEM) analysis demonstrated that the composite impregnation liquid successfully permeates and fills the interior of the poplar cells.

Microstructure and chemical composition of compressed and carbonized poplar

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Study on Poplar Densification by Cross-Grain Compression

Plastic and Elastic Strains in Poplar Wood under High-Pressure Densification

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Dyeing of Poplar Wood Through High-Pressure Processing: Performance Evaluation

Densification of poplar veneer

Chemical modification of poplar wood featuring compressible rebound 3D structure as water treatment absorbents

Effect of thermal treatment with water, H2SO4 and NaOH aqueous solution on color, cell wall and chemical structure of poplar wood

Mechanical Properties and Dimensional Stability of Poplar Wood Modified by Pre-Compression and Post-Vacuum-Thermo Treatments

Effect of temperature on color and chemical composition of poplar powder compacts during warm-press forming

Characterization of Microstructure, Chemical, and Physical Properties of Delignified and Densified Poplar Wood

Research on the Impregnation Process and Mechanism of Silica Sol/Phenolic Resin Modified Poplar Wood

Integrated approach for improving mechanical and high-temperature properties of fast-growing poplar wood using lignin-controlled treatment combined with densification

Preparation of highly-densified modified poplar wood by evacuating the micro-pores of wood through a gas expansion method

Characteristics of Pore Structure in the Evaporated Stage of Wood-Derived Carbon

Studies on the Mechanism of Poplar-wood Flash Pyrolysis Process

Experimental evaluation of combustion performance in the three main anatomical sections of poplar wood

Pyrolysis of Wood Species Based on the Compositional Analysis

Modification Mechanisms and Properties of Poplar Wood via Grafting with 2-Hydroxyethyl Methacrylate/N,N'-methylenebis(acrylamide) onto Cell Walls

Effect of Compression Combined with Steam Treatment on the Porosity, Chemical Compositon and Cellulose Crystalline Structure of Wood Cell Walls