Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Synthesis of stable sols based on titanium dioxide, silicon and metal ion for use in photocatalysis

Study on in-situ Modification of Vinyl Acetate-Acrylate Latex by Anatase TiO2 Sol

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Improving the Stability of Tio2 Aqueous Suspensions by Coupling Tio2 Nanoparticles on Zrp Nanoplatelets

Solvothermal synthesis of stable nanoporous polymeric bases-crystalline TiO2 nanocomposites: visible light active and efficient photocatalysts for water treatment.

A high-stability silica-clay composite: synthesis, characterization and combination with TiO2 as a novel photocatalyst for Azo dye.

Polyhydroxybutyrate-co-hydroxyvalerate/titanium dioxide composite films: green synthesis, characterization, and photocatalytic assessment

Preparation and Photocatalytic Performance of Fixed Titanium Dioxide Film

Obtaining and Properties of a Photocatalytic Composite Material of the “SiO2–TiO2” System Based on Various Types of Silica Raw Materials

Synthesis and electric field response of titanium dioxide nano-particles dispersed in hydrophobic solvents

Influence of Pretreatment of Titanium Substrate on Long-Term Stability of TiO2 Film

Room-Temperature Preparation of TiO2-SiO2 Composite Film and Its Properties

Role of Ammonium Ions on the Stability of TiO2 Sol

Eco-Friendly Colloidal Aqueous Sol-Gel Process for TiO2 Synthesis: The Peptization Method to Obtain Crystalline and Photoactive Materials at Low Temperature

The effect of surfactant-free TiO2 surface hydroxyl groups on physicochemical, optical and self-cleaning properties of developed coatings on polycarbonate

Low-Temperature Preparation of Macroporous Anatase TiO2 Thin Film and Its Photocatalytic Activity

Stoichiometry control and structure evolution in hydrothermally derived (Ba,Sr)TiO3 films

Compatibilization of titanium dioxide powders with non-polar media : Adsorption of anionic surfactants and its influence on dispersion stability

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Controlled Synthesis of Titanium Dioxide Nanostructures

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.