REAL-TIME MEASUREMENT OF VIBRATIONAL PROPERTIES OF GREEN WOOD AT HIGH TEMPERATURE ' Yoshitaka Kubojima
Y. Suzuki,M. Tonosaki
Abstract:To obtain basic data for high-temperature drying of wood, changes in vibrational properties of green wood of Sitka spruce (Picea sitchensis Cam) in a high-temperature atmosphere were measured in situ. Young's modulus and loss tangent were measured with vibration tests in an electric oven. Changes in temperature, moisture content, specific Young's modulus, and loss tangent with time were obtained. These changes were investigated by dividing them into four stages. Kr>ywords: Real-time measurement, vibrational properties, green wood, high-temperature drying. ~NTRODUCTION antee both drying speed and quality of wood There have been many studies on the method to dry wood quickly (Sumi 1978, 1982; Shida 1996; Kubojima et al. 1998; Nakashima et al. 1999; Yoshida et al. 1999; Kubojima and Shida 2001), and high-temperature drying of wood is gradually coming into widespread practice. This is because the high-temperature drying, which makes it possible to dry wood in a short time, is expected to lower drying cost. However, when wood is dried quickly at high temperature, many types of damage such as checks, splits, and honeycombs tend to occur. Therefore, a heating technique to guar' This research was presented in part at the 50th annual meeting of the Japan Wood Research Society in Kyoto, April 2000. products is needed. In order to develop this technique, the change in wood during high-temperature drying should be studied. For this purpose, it is important to understand basic wood properties when water is lost by heating. The wood property that relates to the checks directly is work before rupture, in other words, relationship of stress-strain. Wood deformation under the influence of external force consists of elastic deformation and flow one. One of the wood properties that relates to such wood deformation and can be measured simply in situ is viscoelasticity. We have already measured the viscoelasticity of oven-dried wood specimens with a vibration test while the specimens are heated from room temperature to 200°C (Kubojima et al. 2001). W<iod i i ~ r < / I ih6.r .S<.,<,n< c. 344). 2002. pp 613-h0 c ' 2002 by thr Soctcty 01 Wood Sc~encc and 'Technology 644 WOOL) AND FIBER SCIENCE, OCTOBER 2002, V. 34(4)
Environmental Science,Materials Science