Abstract:A new Q&P processing route, i.e., applying austempering below Ms in normal two-step Q&P route (termed AQ&P), was proposed and applied to a medium-carbon steel. The effects of isothermal transformation at the quenching temperature on the microstructure evolution and mechanical properties of AQ&P steel were investigated. It was found that both the strength and the elongation of the steel were improved using AQ&P processing route. The yield strength and tensile strength were improved by ~ 100 and ~ 160 MPa, respectively, with similar elongation through austempering for 600 s compared to that of specimens treated by normal two-step Q&P route. Therefore, the product of strength and elongation was increased by 18.8% after AQ&P treatment. In addition, the volume fraction of retained austenite was first decreased and then increased with the extension of the quenching time. Compared to a normal two-step Q&P route, the retained austenite decreased about 6% after austempering for 600 s in AQ&P route. Moreover, the medium-carbon steel experienced a continuous martensitic transformation during isothermal holding at the quenching temperature. The phase transformation during isothermal holding includes two stages: quick martensitic transformation and slow bainitic transformation.

Effects of Isothermal Transformation at the Quenching Temperature on the Microstructure and Mechanical Properties of a Medium-Carbon Steel