Synthesis and characterization of mixed oxides derived from lanthanum orthoferrite perovskite: exploring morphological, spectroscopic, and photocatalytic properties
Achouak Achour,Malika Abba,Necira Zelikha,Salah Eddine Hachani,Chahbaoui Narimene,Rahal Rahima,Djoudi Lynda,Menasra Hayet,Khemakhem Hamadi,Achouak AchourMalika AbbaNecira ZelikhaSalah Eddine HachaniChahbaoui NarimeneRahal RahimaDjoudi LyndaMenasra HayetKhemakhem Hamadia Laboratory of Molecular Chemistry and Environment,University of Biskra,B.P.145,Biskra,07000,Algeriab Laboratory of Applied Chemistry,University of Biskra,B.P.145,Biskra,07000,Algeriac Faculty of Technology,Department of Process Engineering and Petrochemistry,University of El Oued,El Oued,39000,Algeriad Laboratory of Multifunctional Materials and Applications (LaMMA),Faculty of Sciences of Sfax,BP 1171,Sfax,3000,Tunisia
DOI: https://doi.org/10.1080/00958972.2024.2330098
2024-03-19
Journal of Coordination Chemistry
Abstract:We synthesized pure and doped gadolinium, samarium, and chromium LaFeO 3 denoted as LFO, LFCO, LGFCO, and LSFCO, respectively, employing a straightforward, cost-effective, and environmentally friendly solid-state method. The resulting samples were characterized through powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy, scanning electron microscopy (SEM), and UV–Visible absorption measurements. The PXRD findings affirmed that the phase structures corresponding to LFO, LFCO, LGFCO, and LSFCO manifested at an identical calcination temperature of 1200 °C, adopting orthorhombic systems. The calculated crystallite size for each sample, employing Debye-Scherrer's equation, ranged from 25 to 37 nm, with LGFCO and LSFCO exhibiting an augmented crystallite size. This enhancement can be attributed to the integration of dopants into the LaFeO 3 lattice, facilitating crystallite growth. SEM images portrayed microstructure composed of fine particle sizes and pseudo-spherical morphology, and the stoichiometry of La, Fe, and O in LFO was confirmed by energy dispersive spectroscopy (EDS). Reduction in the band gap was ascribed to the doping effect, with LGFCO exhibiting the lowest band gap value. Notably, this ceramic material demonstrated the highest photocatalytic activity for methylene blue degradation under sunlight radiation, surpassing the performance of the other examined samples.
chemistry, inorganic & nuclear