Abstract:Degradation mechanisms of 275-nm-band AlxGa1-xN multiple quantum well deep-ultraviolet light-emitting diodes fabricated on a (0001) sapphire substrate were investigated under hard operation conditions with the current of 350 mA and the junction temperature of 105 °C. The optical output power (Po) initially decreased by about 20% within the operating time less than 102 h and then gradually decreased to about 60% by 484 h. For elucidating the causes for the initial and subsequent degradations, complementary electrical, time-resolved photoluminescence (TRPL), and impurity characterizations were carried out making a connection with the energy band profiles. Because the degradation of the wells was less significant than the Po reduction, the initial degradation is attributed essentially to the decrease in carrier injection efficiency (ηinjection), not in internal quantum efficiency of the wells, most likely due to depassivation of initially H-passivated preexisting nonradiative recombination centers (NRCs) in a Mg-doped p-type Al0.85Ga0.15N electron blocking layer. The principal cause for the subsequent Po reduction until 484 h is attributed to further decrease in ηinjection due to the appearance of certain current bypasses in addition to continuous depassivation of the NRCs in p-type AlxGa1-xN layers. According to our database on the species of vacancy-type defects acting as NRCs in GaN and AlN, which have been identified using the combination of positron annihilation and TRPL measurements, vacancy clusters comprised of a cation vacancy (VIII) and nitrogen vacancies (VN), such as VIIIVN2∼4, are the most suspicious origins of the NRCs in Mg-doped p-type AlxGa1-xN layers.

Degradation mechanism beyond device self-heating in high power light-emitting diodes

Theoretical considerations on efficiency degradation due to thermal effect in a planar GaN-based LED with a GaN substrate

Degradation Behaviors of High Power Gan-Based Blue Light Emitting Diodes

Aging characteristics of blue InGaN micro-light emitting diodes at an extremely high current density of 3.5kAcm−2

Anomalous Efficiency Elevation of Quantum-Dot Light-Emitting Diodes Induced by Operational Degradation.

Different Degradation Behaviors of Ingan/Gan Mqws Blue and Violet Leds

Study on the Stability of the High‐brightness White LED

The Electroluminescence Spectra of InGaN/GaN Blue LEDs During Aging Ti Me

Degradation of InGaN/GaN Quantum Well UV LEDs Caused by Short-Term Exposure to Current

Investigation of degradation dynamics of 265 nm LEDs assisted by EL measurements and numerical simulations

Operation-induced degradation mechanisms of 275-nm-band AlGaN-based deep-ultraviolet light-emitting diodes fabricated on a sapphire substrate

Efficiency Droop Behavior of Direct Current Aged GaN-based Blue Light-Emitting Diodes

Examining Degradation Mechanisms in Strain-Relaxed AlGaN-Based UV-C Light-Emitting Diodes Using Raman Spectroscopy

Thermal Properties of Microscale Inorganic Light-Emitting Diodes in a Pulsed Operation

Research on the Current-voltage Characteristics of GaN-based High Power Flip-chip Blue LED

Degradation of Ingan/Gan Leds under Forward-Bias Operations in Salty Water Vapor

On the Temperature Dependence of Electron Leakage from the Active Region of Gainn/Gan Light-Emitting Diodes

Analysis of the Degradation of High Power Light Emitting Diode

Rapid Degradation of InGaN/GaN Green Laser Diodes

The warming-up effects of quantum-dot light emitting diodes: A reversible stability issue related to shell traps

Comparison of Temperature Dependent Electroluminescence of InGaN/GaN and AlGaInP Based LEDs