Synthesis and thermal analysis of poly(methyl methacrylate) oligomer functionalized polyethylene block copolymer

Urmilla Baruah,Maitrayee Saikia,Edja F. Assanvo,Somip Borphukan,Lachit Phukan,Arvind Gautam,Shashi D. Baruah

DOI: https://doi.org/10.1007/s00289-016-1828-7

IF: 2.843

2016-10-13

Polymer Bulletin

Abstract:Living oligomers of methyl methacrylate (MMA) were synthesized photochemically with iron(III) tris(oxalato) ferrate(III) tetrahydrate (Fe[Fe(C2O4)3]·4H2O) as photoinitiator under UV irradiation of 254 nm at 40 °C in dimethyl sulfoxide in the presence of triethylamine as coinitiator. The synthesized oligomers were incorporated in the ethylene chain by reverse atom transfer radical polymerization in N,N′-dimethylformamide using 2,2′-azobisisobutyronitrile as initiator with FeCl3/2,2′-bipyridine (bpy) catalyst system. FT-IR and 1H NMR analysis confirms the incorporation of pre-synthesized poly(MMA) in the ethylene chain. Thermogravimetric analysis of the copolymer shows a three step decomposition process with the major decomposition at approximately 380 °C. Apparent activation energy (Ea) of each step was calculated using non-isothermal methods of Kissinger, Friedeman, Flynn–Wall–Ozawa (FWO) and modified Coats-Redfern (MCR). The Ea value obtained from FWO and MCR methods shows good agreement and the value for the final step of decomposition was calculated to be 235 kJ mol−1. The conversion dependency of decompositions on the process rate can be best explained by Sestak-Berggren model which can be established as f(α)=3.67×102exp-199.28RT(1-α)2.03α3.03\documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$$\begin{aligned} f(\alpha ) = 3.67 \times 10^{2} \exp \left( {\frac{-199.28}{RT}} \right)(1 - \alpha )^{2.03} \alpha^{3.03} \hfill \\ \hfill \\ \end{aligned}$$\end{document} with pre-exponential factor (A) = 3.67 × 102 min−1.

polymer science