Processing and properties of mild interstitial free steels
S. Hoile
DOI: https://doi.org/10.1179/026708300101506902
IF: 1.8
2000-10-01
Materials Science and Technology
Abstract:Over recent years, new interstitial free (IF) steel grades containing controlled low levels of carbon and nitrogen have been adopted to fabricate car body panels. The processing and properties of these steels are reviewed. They can provide very high levels of formability, as indicated by width to thickness strain ratios during forming r of 1.8 (r values of traditional aluminium killed steels rarely exceed 1.8). Typically total interstitial contents are in the region <0.0030 wt-%C and <0.0040 wt-%N. Elimination of these solutes damaging to formability is achieved through careful control of the melt chemistry during steelmaking and by the hyperstoichiometric addition of titanium and/or niobium to react with carbon and nitrogen to form precipitates. Precipitation control during hot mill processing is instrumental in determining the grain size of the hot rolled material, which must be as small as possible, and grain size in the final cold rolled and annealed product, which must be optimised for formability. Control of crystallographic texture is also fundamental in producing exceptional deep drawability. Subsequent casting, rolling, and annealing operations must also be controlled to optimise the development of preferred precipitation and texture. The chemistry is designed such that under equilibrium conditions IF steel should contain no carbon or nitrogen in solid solution. Hot rolling, however, is a process in which equilibrium is not attained, and for this reason it is desirable for the removal of carbon and nitrogen to begin early in the hot rolling process. The most favourable removal mechanism in this respect is the precipitation of titanium carbosulphide (titanium carbide and niobium carbide also proliferate, but precipitate out at lower temperatures). Titanium carbosulphide formation is favoured when the slab reheat temperature is <1200°C, and when the C/S ratio approaches stoichiometric. Optimum finishing temperatures are close to the Ar 3 temperature but practically it is advisable to increase the finishing temperature by 20–30 K above Ar 3 to avoid the risk of ferritic rolling taking place at the edges of the strip. For high formability in the final product, fast cooling on the runout table is required to prevent excessive grain growth. For titanium only containing IF steels, coiling temperature dependency is small; thus the favoured coiling temperature is low (∼625°C) to obviate the need for aggressive scale removal techniques. Coiling temperature dependence in niobium containing IF steels is greater, and precipitate coarsening is required to aid recrystallisation during annealing, which may be carried out at up to 50 K higher than in titanium IF steels; thus coiling temperatures are usually >700°C. High reductions, up to approximately 90%, in the cold mill are the key to deep drawability. Annealing temperature is instrumental in determining final drawability providing the Ac 3 temperature has not been exceeded. Time at temperature is also an important factor enabling grain growth to occur, optimising formability.
materials science, multidisciplinary,metallurgy & metallurgical engineering