Abstract:Fe-Zn alloys for degradable vascular stents were prepared via electrodeposition technique. The effect of the concentration of the complexing agent sodium citrate (C 6 H 5 Na 3 O 7 ·2H 2 O) in the plating solution on the solution state, alloy composition, and microstructure was investigated. The complexation mechanism of Fe 3+ , Fe 2+ and Zn 2+ by C 6 H 5 Na 3 O 7 ·2H 2 O was analyzed using cyclic voltammetry. In vitro degradation properties of the alloy were evaluated through electrochemical and static immersion methods. Results showed that an increase of C 6 H 5 Na 3 O 7 ·2H 2 O concentration led to a decrease in pH change of the plating solution, deposition rate, and cathodic current efficiency. With increasing concentration of C 6 H 5 Na 3 O 7 ·2H 2 O, the reduction potential of Zn 2+ gradually shifted positively while the reduction potential difference with Fe 2+ decreased; this resulted in increased Zn content in the alloy and reduced grain size indicating promotion of co-deposition by C 6 H 5 Na 3 O 7 ·2H 2 O. However, excessive sodium citrate caused an increase in the reduction potential difference between Fe 2+ and Zn 2+ leading to decreased Zn content as well as coarsened grains suggesting significant influence on alloy composition from complexing agent concentration. Alloys with different compositions exhibited a single α(Fe) phase with a (211) preferred orientation crystal plane. Polarization curves, electrochemical impedance spectra, and long-term immersion experiments indicated that the corrosion sensitivity of the alloys increased and the corrosion rate elevated with an increase in Zn content in the alloys. These results indicate that reasonable control over the complexing agent, C 6 H 5 Na 3 O 7 ·2H 2 O, is expected to obtain Fe-Zn materials for biodegradable stents with good microstructure and performances.

Effect of citrate additive on the electrodeposition and corrosion behaviour of Zn–Co alloy

Effect of sodium citrate on the electrodeposition of biodegradable Fe-Zn alloys

Microstructural Characterization and Corrosion Behaviors of Ni-Cu-Co Coatings Electrodeposited in Sulphate-Citrate Bath with Additives

Induced Codeposition of Tungsten with Zinc from Aqueous Citrate Electrolytes

Effects of Al content on microstructure and corrosion behavior of Zn-Al alloy coatings

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

Effect of cobalt content on electrodeposition and properties of Co–Ni alloy thin films

Influence of applied potential on tin content in electrodeposition of Zn–Sn alloy coatings and its effect on corrosion protection

Study on effect of different complexing agents and inhibitors on Co corrosion in H2O2 based alkaline solution by EQCM

Electrodeposition of Nanostructured Co–Cu Thin Alloy Films on to Steel Substrate from an Environmentally Friendly Novel Lactate Bath under Different Operating Conditions

Effect of Electroplating Bath Composition on Corrosion Resistance of Deposited Cobalt Films

Electroplating and Physicochemical Properties of Zinc–Nickel Alloy Coatings from Ammonium Oxalate Electrolytes

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

The Performance of Zn-Ni Alloy Coating Electrodeposited from Stabilized Bath

Study of Electroless Ni-Zn-P Alloy Plating from Acidic Bath

Electrodeposition and characterization of Zn–Sn alloy coatings from a deep eutectic solvent based on choline chloride for corrosion protection

Electroplating of Nanocrystalline Ni–Co Alloys Using Cysteine and Their Electrochemical Behaviour in NaOH Solution

Electrodeposition, Morphology, Composition, and Corrosion Performance of Zn-Mn Coatings from a Deep Eutectic Solvent

Effect of Sodium Citrate and Sodium Carbonate Complexing Agents on Electroless Ni-Sn-P Coating on Magnesium Alloy

Influence of the Contents of Refractory Components on the Corrosion Resistance of Ternary Alloys Based on Iron and Cobalt

Effect of Α-Al2o3 Particles on the Electrochemical Codeposition of Co–Ni Alloys from Sulfamate Electrolytes