Effect of thermomechanical processing on evolution of various phases in Ti–Nb–Zr alloys

M. Geetha,A.K. Singh,A.K. Gogia,R. Asokamani

DOI: https://doi.org/10.1016/j.jallcom.2004.04.113

IF: 6.2

2004-12-01

Journal of Alloys and Compounds

Abstract:This paper describes the effect of thermomechanical processing on microstrucural evolution of three alloys, namely Ti–13Nb–13Zr (T1), Ti–20Nb–13Zr (T2) and Ti–20Nb–20Zr (T3), with an objective to develop equiaxed microstructure in all three alloys by subjecting them to appropriate hot-rolling conditions. The alloys were hot-rolled in α + β phase field and then subjected to various heat treatments. Samples from the hot-rolled alloys were subjected to solution treatment (ST) in β and α + β phase fields, respectively, and subsequently aged at different temperatures for the same time interval. Phases evolved on various treatments were studied using X-ray diffraction (XRD), optical microscope and electron probe microscope techniques. The micrographs of the hot-rolled samples of T2 and T3 alloys reveal fine equiaxed structure; on the other hand, a mixture of equiaxed and elongated α phase is observed in alloy T1. X-ray diffraction analysis of the β ST and water-quenched samples clearly exhibits the formation of α′ in T1 alloy and, α′, α″ and β phases in T2 and T3 alloys. However, α″ phase is observed for T1 alloy only in α + β ST condition. X-ray diffraction analysis of T3 sample subjected to β ST and aging at 400°C reveals the presence of ω phase. The presence of higher amount of Nb and Zr should have resulted in the formation of ω phase in the T3 alloy at low-temperature aging.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering