Abstract:<p class="a-plus-plus">The continuous casting of Ti-alloyed Al-killed steels traditionally experiences clogging in the tundish, impeding stable operation. We studied the microstructures and mode of formation of such clogging deposits in tundish skulls recovered after long cast series. We sampled the steel skull along the whole tundish bottom from under the ladle shroud (impact zone) up to the tundish well and nozzle. The microstructures imply that the steel solidifies to the refractory (gunning mass) and remains partially solid through the entire cast. Thus, a "mushy zone" of steel loaded with solid delta ferrites is present along the margins of the steel during casting. In this mushy zone, the widely observed clusters of variably sintered alumina (NMI) accumulate, along with a substantial amount of gas bubbles acting as inclusion scavengers. The clustered alumina particles show a lognormal particle size distribution (PSD) in all locations, which becomes more pronounced if correcting for the observable sintering. Sintering of alumina size distributions linearizes a PSD, and further evolution, once the deposit is locked in place, occurs by Ostwald ripening, introducing skewness to the distributions. The observed PSDs contrast with the established log-linearity of PSDs of individual floating alumina NMI in the bulk steel, and suggest that the source of the alumina in the clogging deposits is not the passing bulk steel. However, ubiquitous sedimentary features show that the alumina particles are also not grown by reoxidation <em class="a-plus-plus">in situ</em>. An upstream source separate from the bulk stream must be inferred, which is also required by the consistent sporadic presence of oxidic materials which cannot be derived from local sidewall reaction. In summary, the development of clogging deposits in this type of steel is an example of "slurry casting" of partially solidifying steel over thermal loss surfaces of refractories in the nozzle area.</p>

Skin holes of titanium casting

Castability and surface hardness of titanium cast plates obtained from experimental phosphate-bonded silica investment molds

Interface Reaction During Titanium Alloys Investment Casting by Residue Gas in Ceramic Mold

The Preparation of the Multilevel Holes and Analysis of the Pure Titanium Surface

New process solutions in the manufacture of thermochemically resistant ceramic molds for casting titanium alloys

Effect of pressure difference on the quality of titanium casting

New Technological Solutions in the Manufacture of Thermochemically Resistant Ceramic Molds for Casting Titanium Alloys

Reaction of Titanium Investment Castings Made by Zr(CH3COO)2-Y2O3 Shell

Effect of SiO 2 Concentration in Silica Sol on Interface Reaction During Titanium Alloy Investment Casting

Fracture Behavior of a High Pressure Die Casting AlSi10MnMg Alloy with Varied Porosity Levels

Reaction of titanium investment castings made by Zr(CH 3 COO) 2 -Y 2 O 3 shell

Effect of Mold Material and Binder on Metal-Mold Interfacial Reaction for Investment Castings of Titanium Alloys

Three-dimensional investigation of void growth leading to fracture in commercially pure titanium

Towards High-Quality Investment Casting of Ti-6Al-4V with Novel Calcium Zirconate Crucibles and Optimized Process Control

In Situ Elimination of Pores During Laser Powder Bed Fusion of Ti–6.5Al–3.5Mo–l.5Zr–0.3Si Titanium Alloy

Titanium casting into phosphate bonded investment with zirconite.

INTERACTION OF CHEMICALLY ACTIVE MELTS WITH CERAMIC MOLD MATERIALS IN VACUUM

Quantitative study of geometric characteristics and formation mechanism of porosity defects in selective laser melted Ti6Al4V alloy by micro-computed tomography

Corrosion resistance of calcium zirconate crucible to titanium-copper melts

[Studies on application of pure titanium for cast plate]

Microstructures and Formation of Tundish Clogging Deposits in Ti-Alloyed Al-Killed Steel