Abstract:Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science, Ahead of Print. This paper investigates the correlation between the surface quality and the cross-sectional quality, microstructure, internal defects, and mechanical properties of specimens formed by selective laser melting (SLM) under different scanning speeds and scanning intervals. Therefore, different machining parameters were chosen to prepare titanium alloy specimens by SLM technique. The surface morphology of the specimens was characterized using a light microscope, and the surface quality, microstructure, internal defects, and deep connection of the mechanical properties of the specimens formed under different parameters were investigated. In addition, numerical simulation of the melt pool morphology under different scanning speeds was used. The results show that there is a strong correlation between the surface quality of the specimen and the section quality and mechanical properties. When the scanning speed is 350 mm/s, the surface roughness is 14.7 μm, the density is 99.99%, the tensile strength and yield strength are 1209 and 1151 Mpa respectively, and the surface quality, cross-sectional quality and mechanical properties all tend to deteriorate as the scanning speed increases. When the scanning interval is 0.11 mm, the mechanical properties of surface quality and cross-sectional quality are optimal, the surface roughness is 14.5 μm, and the density reaches 99.99%, at this time, the microscopic needle martensite α′ phase is uniformly distributed and refined, and its mechanical properties are optimal, the tensile strength is 1239 MPa, and the internal hole defects are less. Numerical simulations of a single track melt pool show that the depth of depression caused by the recoil pressure is larger and the melt pool is deeper when the scanning speed is 350 mm/s. Therefore, it has better fluidity and ductility. Simulation results of the double tracks show that when the scanning interval is 130 μm, a large amount of incompletely melted powder at the midline of the double track does not lap well, which leads to the formation of pore defects inside the specimen. The above simulation results are highly consistent with the surface quality of the specimens during the experiments, which provides a guide to analyze the connection between the melt pool evolution and the Ti6Al4V molding quality.

Quantitative study of geometric characteristics and formation mechanism of porosity defects in selective laser melted Ti6Al4V alloy by micro-computed tomography

Study of pore defect and mechanical properties in selective laser melted Ti6Al4V alloy based on X-ray computed tomography

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Evolution of multi pores in Ti6Al4V/AlSi10Mg alloy during laser post-processing

X-ray CT analysis of the influence of process on defect in Ti-6Al-4V parts produced with Selective Laser Melting technology

Numerical Study of the Pore Defects Formation Mechanisms in Selective Laser Melting Process

Effects of Defects and Microstructures on Tensile Properties of Selective Laser Melted Ti6Al4V Alloys Fabricated in the Optimal Process Zone

Effects of Embedded Spherical Pore on the Tensile Properties of a Selective Laser Melted Ti6Al4V Alloy

Porosity effect on tensile behavior of Ti-6Al-4V specimens produced by laser engineered net shaping technology

Use of X-ray Computed Tomography for Assessing Defects in Ti Grade 5 Parts Produced by Laser Melting Deposition

Defect formation mechanism of laser additive manufacturing joint for large-thickness Ti6Al4V titanium alloy with Y2O3 nanoparticles

The effect of porosity on the mechanical properties of Ti-6Al-4V components manufactured by high-power selective laser melting

Study on the mechanism of correlation between surface quality and tissue properties of Ti6Al4V alloy formed by selective laser melting

Effect of Defects on High Cycle Fatigue Property of Selective Laser Melted Ti6Al4V Alloy

Defect Induced Fatigue Behaviors of Selective Laser Melted Ti-6Al-4V Via Synchrotron Radiation X-Ray Tomography

Influence of Modified Microstructures and Characterized Defects on Tensile Properties and Anisotropy of Selective Laser Melting-Produced Ti6Al4V Alloys

In Situ X-ray Micro-Computed Tomography Study of the Damage Evolution of Prefabricated Through-Holes in SLM-Printed AlSi10Mg Alloy under Tension

Influence of Laser Post-Processing on Pore Evolution of Ti–6Al–4V Alloy by Laser Powder Bed Fusion

Discovering the role of the defect morphology and microstructure on the deformation behavior of additive manufactured Ti–6Al–4V

Mechanical Properties of Porous Ti-6Al-4V Titanium Alloys Fabricated by Selective Laser Melting