Abstract:Electron beam selective melting (EBM) and selective laser melting (SLM) are regarded as significant manufacturing processes for near-net-shaped Ti6Al4V components. Generally, in the conventional EBM process, preheating is necessitated to avoid “smoke” caused by the charging of electrons. In the conventional SLM process, laser as an energy source without the risk of “smoke” can be employed to melt metal powder at low temperatures. However, because of the low absorption rate of laser, the powder bed temperature cannot reach a high level. It is difficult to obtain as-built TiAl4V with favorable comprehensive properties via conventional EBM or SLM. Hence, two types of electron beam and laser hybrid preheating (EB-LHP) combined with selective melting strategies are proposed. Using laser to preheat powder allows EBM to be performed at a low powder bed temperature (EBM-LT), whereas using an electron beam to preheat powder allows SLM to be performed at a high powder bed temperature (SLM-HT). Ti6Al4V samples are fabricated using two different manufacturing strategies (i.e., EBM-LT and SLM-HT) and two conventional processes, i.e., EBM at a high powder bed temperature (EBM-HT) and SLM at a low powder bed temperature (SLM-LT). The temperature-dependent surface quality, microstructure, density, and mechanical properties of the as-built Ti6Al4V samples are characterized and compared. Results show that EBM-LT Ti6Al4V exhibits a higher ultimate tensile strength (981±43 MPa) and a lower elongation (12.2%±2.3%) than EBM-HT Ti6Al4V owing to the presence of α′ martensite. The SLM-HT Ti6Al4V possesses the highest ultimate tensile strength (1,059±62 MPa) and an elongation (14.8%±4.0%) comparable to that of the EBM-HT Ti6Al4V (16.6%±1.2%).

A study of the microstructures and mechanical properties of Ti6Al4V fabricated by SLM under vacuum

Effects of HIP Process Parameters on Microstructure and Mechanical Properties of Ti-6Al-4V Fabricated by SLM

Tensile Behavior of Ti-6Al-4V Alloy Fabricated by Selective Laser Melting: Effects of Microstructures and As-Built Surface Quality

Study of pore defect and mechanical properties in selective laser melted Ti6Al4V alloy based on X-ray computed tomography

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Experimental Study of Performance of Ti-6Al-4V Femoral Implants Using Selective Laser Melting (SLM) Methodology

A detailed analysis on the microstructure and compressive properties of selective laser melted Ti6Al4V lattice structures

Microstructure and Mechanical Properties of Ti-6Al-4V Manufactured by Selective Laser Melting after Stress Relieving, Hot Isostatic Pressing Treatment, and Post-Heat Treatment

Comparison of the microstructures and mechanical properties of Ti–6Al–4V fabricated by selective laser melting and electron beam melting

Microstructure, Mechanical Properties, and Constitutive Models for Ti–6Al–4V Alloy Fabricated by Selective Laser Melting (SLM)

Microstructure and inclusion of Ti–6Al–4V fabricated by selective laser melting

Microstructure and mechanical deformation behavior of selective laser melted Ti6Al4V ELI alloy porous structures

Microstructural and mechanical optimization of selective laser melted Ti6Al4V lattices: Effect of hot isostatic pressing

Effects of heat treatment and hot isostatic pressing on microstructure and fatigue improvements in Ti-6Al-4V alloy fabricated by selective laser melting

Performance of Ti6Al4V fabricated by electron beam and laser hybrid preheating and selective melting strategy

Microstructural Characteristics and Material Failure Mechanism of SLM Ti-6Al-4V-Zn Alloy

Dense layer, microstructure, and mechanical performances of Ti–6Al–4V alloy prepared by metal injection molding

Uniaxial Compression Properties and Compression Fatigue Performance of Selective Laser Melted Ti–6Al–4V Cellular Structure

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Effect of heat treatment on the corrosion resistance behavior of selective laser melted Ti6Al4V ELI

The Low-Cycle Fatigue Behavior, Failure Mechanism and Prediction of SLM Ti-6Al-4V Alloy with Different Heat Treatment Methods