Structural evolution and its influence on electrical properties of lithium doped alkali niobates at different sintering temperatures

Haobam Samananda Singh,Irom Monika Aniz,Chiranjit Chaliha,Mamata Maisnam

DOI: https://doi.org/10.1007/s10854-024-13493-5

2024-09-30

Journal of Materials Science Materials in Electronics

Abstract:The processing techniques of the ceramics have a sensitive impact on the structural and electrical characteristics. Effective sintering temperature contributes to the attractive properties of the ceramics. The piezoelectric ceramics with chemical formula K 0.47 Na 0.47 Li 0.06 NbO 3 were prepared and sintered at different temperatures (viz. 950 °C for 5 min and 850 °C for 4 h, 1000 °C for 5 min and 900 °C for 4 h, 1050 °C for 5 min and 950 °C for 4 h, and 1100 °C for 5 min and 1000 °C for 4 h) using two-step sintering technique. ZnO (1 wt%) was used as a sintering aid. When sintered at elevated temperatures, the orthorhombic phase of the sample changes to a tetragonal phase, according to the X-ray diffraction analysis. The unit cell structures, crystallite sizes, lattice strain, and octahedral tilting observed are studied from X-ray diffraction analysis. Room temperature electrical analysis of the samples shows the dispersive behaviour of the dielectric constant and impedance when examined in the frequency range 20 Hz to 10 MHz. The dielectric constant elevates with the rise in sintering temperature whereas the impedance shows a declining pattern as the sintering temperature rises. The effects of various structural properties on the electrical properties are presented in the paper. The a.c. conductivities of the samples are measured in the frequency range 20 Hz to 10 MHz and the Nyquist impedance plots for the samples are studied to understand the conduction mechanism.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied