From batch to flow: the effect of pH, current, and the crystal facets of Cu2O on electrochemical CO2 reduction
Mathias van der Veer,Nick Daems,Pegie Cool,Tom Breugelmans
DOI: https://doi.org/10.1039/d4se00130c
IF: 6.813
2024-05-10
Sustainable Energy & Fuels
Abstract:As humanity is confronted by climate change, electrochemical CO 2 reduction has become an important strategy for generating value-added chemicals whilst lowering carbon emissions. In this work, Cu 2 O nanoparticles with different morphologies and predominant exposed crystal facets, including nanocubes (Cu 2 O-NC) with (100) facets, nanoflowers (Cu 2 O-NF) with (110) facets, and octahedral structures (Cu 2 O-O) with (111) facets, are prepared, and compared as catalysts for the electrochemical CO 2 reduction to C 2+ products in a flow cell electrolyzer, to overcome the mass transfer limitations of CO 2 in an H-cell and reach industrially relevant currents. To maximize the performance towards C 2+ products, a parameter optimization ( i.e. pH and current) was performed. Under the conditions of 150 mA cm −2 and pH of 8.5, the Cu 2 O-NC revealed a maximum faradaic efficiency of 58% for C 2+ products. Similar studies in an H-cell system have shown lower total C 2+ FE of around 35–40% for the nanocubes, indicating an improvement and showcasing the advantages of using a gas-fed flow electrolyzer. Finally, the long-term stability of these materials was also evaluated. The results revealed that C 2+ activity remains constant for four hours at 50%. However, a sharp decline was observed after five hours when GDE flooding occurs, leading to a dominant HER. To confirm, the electrode was washed and dried before re-utilizing it. Since the Cu 2 O largely recovers its initial C 2+ activity (from 50% to 43%) albeit with a slightly different product composition, this confirms GDE flooding as the main cause of degradation. During the eCO 2 RR, Cu 2 O is reduced to metallic Cu, as proven by in situ Raman. As a result, the particle morphology is roughened, which is proven by ex situ SEM images. Subsequently, water penetrates the gas diffusion electrode more easily, inhibiting the diffusion of CO 2 , and alongside the electrowetting effect results in GDE flooding. In conclusion, this work explores the utilization of different Cu 2 O catalysts in a flow electrolyzer, revealing insights into higher currents, their stability issues, crystal facet dependency, and reaction environment, which was unexplored in previous literature where the focus was on H-cell testing, which evaluates the catalysts under less demanding and more controlled conditions that are less relevant for up-scaling and eventual commercialization. Based on these new insights, further improvements can be made to enhance the total C 2+ FE and improve stability.
materials science, multidisciplinary,chemistry, physical,energy & fuels