Abstract:Thin-gauge non-oriented silicon steel with high strength was successfully processed using strip casting. Texture evolution and strengthening mechanism via nanoscale Cu-rich precipitates were studied to fundamentally understand the balanced combination of magnetic properties and mechanical properties. Coarse equiaxed grains with average size of ∼190 μm and relatively random texture were formed in the as-cast strip, which contributed to the inhomogeneous deformation, resulting in high density of shear bands. Exact Cube was retained from the initial Cube texture and new Goss was formed during the heavy rolling process in the 0.20 mm cold rolled sheet, which promoted relatively strong Cube and Goss texture after recrystallization annealing. The 0.20 mm annealed sheet exhibited high magnetic induction of 1.709 T, which corresponds to the high texture factor of 0.5. The total iron losses were significantly reduced with decrease in thickness, and the P1.5/50, P1.0/400, and P1.0/1000 in 0.20 mm sheet were as low as 2.63, 15.17 and 55.63 W/kg, respectively, which showed a good match between magnetic induction and iron loss. During the aging process, both the magnetic induction and total iron loss exhibited relatively good stability. With increase in aging time, the yield strength first rapidly increased and then slightly decreased. In 0.20 mm sheet, peak yield strength of ∼630 MPa was obtained on aging at 550 °C for 90–120 min. The key mechanism of precipitation strengthening was attributed to the difference in modulus and coherency strain associated with high density of nanoscale precipitates of ∼5 nm. The study revealed that the nanoscale Cu-rich precipitates can be adopted as effective approach to increase the yield strength over ∼100 MPa without deteriorating iron loss in thin-gauge non-oriented silicon steel by strip casting, which guaranteed the balance of magnetic properties and mechanical properties to meet the requirements of high-speed motor.

High-strength low-iron-loss electrical steel accomplished by Cu-rich nanoprecipitates

Improvement of magnetic properties via normalizing annealing for high-strength Fe-4.5wt.%Si electrical steel

High‐Strength Nonoriented Electrical Steel with Excellent Magnetic Properties Accomplished by Cu–Ni Multialloying

Magnetic Performance Improvement Caused by Tensile Stress in Equivalent Iron Core Fabricated by High-Strength Non-Oriented Electrical Steel

Effects of Cu Content on Mechanical and Magnetic Properties of High‐Strength Nonoriented Silicon Steel

Ultrastrong and Ductile Soft Magnetic High‐Entropy Alloys via Coherent Ordered Nanoprecipitates

A Novel FeCoNiCr0.2Si0.2 High Entropy Alloy with an Excellent Balance of Mechanical and Soft Magnetic Properties

Microstructure Characteristics and Strengthening Behavior of Cu-Bearing Non-Oriented Silicon Steel: Conventional Process versus Strip Casting

Thin-gauge non-oriented silicon steel with balanced magnetic and mechanical properties processed by strip casting

A novel Fe-Co-Ni-Si high entropy alloy with high yield strength, saturated magnetization and Curie temperature

A Novel Ultrafine-Grained High Entropy Alloy with Excellent Combination of Mechanical and Soft Magnetic Properties

Recent development of advanced precipitation-strengthened Cu alloys with high strength and conductivity: A review

High strength and high conductivity Cu alloys: A review

Dual Nanoprecipitation and Nanoscale Chemical Heterogeneity in a Secondary Hardening Steel for Ultrahigh Strength and Large Uniform Elongation

Super cold‐drawing ability and high tensile strength of Fe35Ni35Cr20Mn10 high‐entropy alloy wires

Development of High-Strength Low-Density Steel for Emerging Lightweight Electric Vehicle Technologies

Novel Strength-Electrical Conductivity Synergy in Cu-based Composites Reinforced with TiZrNbTa High Entropy Alloy

Design and Characterization of Ultrahigh Strength Dual-Phase Steel with Low Ratio of Yield Strength/Ultimate Tensile Strength

Microstructural evolution and properties of a Cu-Fe-Mn-P alloys with high strength and high conductivity

Characteristics,Preparation and Research Progress of High Silicon Electrical Steel