A Novel High-Mn Duplex Twinning-Induced Plasticity Lightweight Steel with High Yield Strength and Large Ductility
Huihui Zhi,Jinshan Li,Lulu Li,Yihua Luo,Yanjing Su,Minjie Lai
DOI: https://doi.org/10.1016/j.jmrt.2024.09.198
2024-01-01
Abstract:In this study, we report a novel high-Mn Fe-21Mn-6Al-4Si-1C (wt.%) duplex lightweight steel with concurrent chemical ordering and twinning-induced plasticity effects. This steel is capable of achieving an exceptional combination of strength and ductility following either cold-rolling and annealing at 1000 degrees C or subsequent short-term aging at 550 degrees C. In its as-annealed state, this steel primarily consists of gamma-austenite and alpha-ferrite, with alpha-ferrite appearing as dispersed particles within fully recrystallized gamma grains. Furthermore, L ' 1(2)- and D0(3)-type ordered nanodomains exist within these two phases, respectively. The aging treatment negligibly affects the size and volume fraction of both the gamma-austenite and alpha-ferrite, yet it enhances the degree of ordering as well as the size and volume fraction of their ordered nanodomains, leading to a rise in yield strength from similar to 800 to similar to 1062 MPa and a decline in total elongation from similar to 60.4% to similar to 44.4%. The high yield strength of this steel originates from multiple strengthening mechanisms involving dislocation interactions with solute atoms, ordered nanodomains, gamma grain boundaries and gamma/alpha phase boundaries. This steel plastically deforms via planar slip during the initial stages. The rather small gamma grain size, coupled with the presence of hard alpha-ferrite particles, fosters the dynamic slip band refinement (DSBR) effect, thereby enhancing the flow stress sufficiently to trigger deformation twinning in the steel during the later stages. The DSBR effect, combined with the progressive formation of deformation twins, stacking faults and Lomer-Cottrell locks, imparts pronounced strain hardenability to this steel, leading to its outstanding ductility.