Organic‐Inorganic Dual‐Network Composite Separators for Lithium Metal Batteries

Zetong Liu,Pingan Li,Kangjia Hu,Hao Sun,Rongxing Li,Shanshan Yang,Xianluo Hu

DOI: https://doi.org/10.1002/marc.202400644

IF: 5.006

2024-10-16

Macromolecular Rapid Communications

Abstract:Ultra‐long HAP nanowires are modified on a high‐porosity PMIA membrane, forming an interconnected dual‐network structure that facilitates efficient ion transport. Through "ion flow redistribution" and restriction of anion transport, this structure promotes uniform lithium deposition and stripping. Consequently, the HAP/PMIA composite separator effectively retards lithium dendrite growth, enhancing the lifespan of lithium metal batteries. The suboptimal ionic conductivity of commercial polyolefin separators exacerbates uncontrolled lithium dendrite formation, deteriorating lithium metal battery performance and posing safety hazards. To address this challenge, a novel organic‐inorganic composite separator designed is prepared to enhance ion transport and effectively suppress dendrite growth. This separator features a thermally stable, highly porous poly(m‐phenylene isophthalamide) (PMIA) electrospun membrane, coated with ultralong hydroxyapatite (HAP) nanowires that promote "ion flow redistribution." The synergistic effects of the nitrogen atoms in PMIA and the hydroxyl groups in HAP hinder anion transport while facilitating efficient Li+ conduction. Meanwhile, the optimized unilateral pore structure ensures uniform ion transport. These results show that the 19 μm‐thick HAP/PMIA composite separator achieves remarkable ionic conductivity (0.68 mS cm−1) and a high lithium‐ion transference number (0.51). Lithium symmetric cells using HAP/PMIA separators exhibit a lifespan exceeding 1000 h with low polarization, significantly outperforming commercial polypropylene separators. Furthermore, this separator enables LiFePO4||Li cells to achieve an enhanced retention of 97.3% after 200 cycles at 1 C and demonstrates impressive rate capability with a discharge capacity of 72.7 mAh g−1 at 15 C.

polymer science