Abstract:A range of Fe-Cr-Ni alloys are used in nuclear power plants due to their high mechanical strength and corrosion resistance. As a major component of these alloys, Ni contributes to the formation of austenite microstructures. In many nuclear reactor applications the alloys are exposed to ionizing radiation (g-rays) that can continuously decompose water to a range of highly redox active species (such as •OH, H2O2, O2). The change in water chemistry induced by radiation can affect both the general and localized corrosion behaviour of these alloys. In particular, its influence on the susceptibility of an alloy to localized corrosion such as crevice and stress corrosion cracking (SCC) are important for assessment of reactor component aging. As well, corrosion products that dissolve into the reactor coolant can be transported to the reactor core where they can be neutron activated. This can create a radiological hazard for reactor maintenance personnel. Thus, quantifying the rate of general corrosion and the corrosion product transport in a reactor are important safety, operation and maintenance issues. It has been well established that the type of oxide that forms on a surface is a critical factor in determining both general and localized corrosion behaviour. Both alloy composition and water chemistry affect the type of oxide that forms. Systematic studies that examine the effect of alloy composition on corrosion are rare and those available have been conducted mostly from a metallurgical perspective. There are even fewer studies that examine the combined effects of alloy composition and corrosion environment. A fundamental understanding of the mechanism by which the Fe to Ni ratio in a steel alloy influences the corrosion rate in different environments will provide valuable information that can be used for alloy selection and usage. We have investigated the effect of the Fe to Ni ratio of alloy on oxide formation and growth kinetics. For this study, customized steel alloys with different Ni contents and constant Cr content (18 ± 1 %) were prepared. The Ni content ranged from 15 to 25 wt.%, within the range between AISI 316L and Alloy 800 (Fig. 1). The corrosion kinetics was investigated using a combination of coupon corrosion tests and electrochemical measurements. These measurements were augmented by oxide surface and depth analyses using several spectroscopic and imaging techniques, and by post-test solution analyses for dissolved metal loss. We found that the oxide formed at pH 10.6 and 80 °C has a graded layer structure, consisting of a mixed spinel oxide (FeCr2O4/Fe3O4/NiFe2O4) as an inner layer and Ni(OH)2 as an outer layer. The increase in Ni content from 15 to 25 wt.% does not affect the inner layer but increases the thickness of the Ni(OH)2 layer. The increase in Ni content also decreases the total amount of dissolved metal loss. Gamma-irradiation of the corroding system increases the corrosion potential on these alloys. Correspondingly, gamma-radiation accelerates the formation of passive oxide layers and decreases the overall rate of metal dissolution. The observed kinetics of oxide growth and metal dissolution can be explained by the competition kinetics of oxide growth and dissolution for oxidized metals. Figure 1

Influence of Ni on corrosion and trench formation of low alloy steel in low H2S content sour corrosion environments

Influence of Ni Addition on Corrosion Performance of Medium-temperature Filler Metal with Low Cu Content for Al Brazed Joints

Corrosion of Nickel in Acid Solutions with Hydrogen Sulphide

Effect of Ti Microalloying on the Corrosion Behavior of Low-Carbon Steel in H2S/CO2 Environment

Corrosion Behavior of AISI 316L Stainless Steel in a Highly Sour Environment

The influence of Ni on the microstructure and corrosion resistance of high-strength low alloy steel in the Cl-containing environment

Effect of Ni on the oxidation behavior of corrosion products that form on low alloy steel exposed to a thin electrolyte layer environment

Insights into the Electrochemical Corrosion Behavior and Mechanism of Electroless Ni-P Coating in the CO2/H2S/Cl− Environment

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment

Time-dependent corrosion behavior of electroless Ni–P coating in H2S/Cl− environment

Study on the role of niobium in corrosion mechanism of low-alloy pipeline steel in H 2 S-saturated solution

Influence of Nitrogen Content on the Corrosion Behavior of Powder Metallurgy Nickel-Free Austenitic Stainless Steel

Elemental sulfur corrosion of nickel-based alloy 825 in CO 2 -H 2 S-containing environment at high temperature and high pressure

The influence of surface oxides on the distribution and release of nickel from Nitinol wires

Effect of Nickel Content on the Corrosion Behaviour of Stainless Steel at 80 °C

The inhibition effects of Cu and Ni alloying elements on corrosion of HSLA steel influenced by Halomonas titanicae

Effects of Adding CO2 to Low Level H2S Containing Aqueous Environments on the Corrosion and Hydrogen Penetration Behaviors of High-Strength Steel

Comprehending the role of the S-phase on the corrosion behavior of austenitic stainless steel exposed to H2S/CO2-saturated liquid and vapor environments

Effect of nitrogen on the corrosion behavior of high-strength low-alloy steel in simulated marine atmosphere

Clarifying the effect of Cu element on the corrosion properties of Ni-Mo low alloy steel in marine environment