Thermal cycling behavior of Srx(Zr0.9Y0.05Yb0.05)O1.95+x thermal barrier coatings by suspension plasma spraying
Xueying Feng,Yu Bai,Yuanming Gao,Jiong Liu,Fei Zheng,Rongxing Li,Wen Ma
DOI: https://doi.org/10.1111/jace.20088
IF: 4.186
2024-08-23
Journal of the American Ceramic Society
Abstract:1. Srx(Zr0.9Y0.05Yb0.05)O1.95+x‐NiCoCrAlY thermal barrier coatings (TBCs) [SZYY‐1, x = 1.0; SZYY‐2, x = 0.9; SZYY‐3, x = 0.8] were deposited by suspension plasma spraying (SPS) using the corresponding precursors suspension prepared by co‐precipitation. 2. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of 1121°C‐1 h high‐temperature thermal cycling, up to 345 times. 3. The effects of microstructure and phase composition on thermal cycling failure of the coating at high temperatures were studied in detail. A finite element model was also proposed to evaluate the thermal stress thermally grown oxide (TGO) morphology of a real coating at different thermal cycling stages. The thermal barrier coatings (TBCs) consisting of Srx(Zr0.9Y0.05Yb0.05)O1.95+x were prepared using the suspension plasma spraying (SPS) method. Precursor suspensions were prepared via co‐precipitation for this purpose. Detailed microstructural, phase composition, and phase content analyses were conducted on these coatings, designated as SZYY‐1 (x = 1.0), SZYY‐2 (x = 0.9), and SZYY‐3 (x = 0.8). Additionally, the coatings underwent a thermal cycling test at 1121°C for 1 h. To assess the morphology of thermally grown oxide (TGO) in a real coating, a finite element model was employed. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of thermal cycling, up to 345 times. The thermophysical high‐temperature properties of the coating can be effectively improved through suitable second‐phase content. Microstructural and finite element analyses revealed that stress, primarily caused by the continuous growth of the Co3O4, NiO and Spinel (CNS) layer within TGO, was the predominant factor leading to coating failure. At elevated temperatures, transverse cracks formed at the interface between the bond coating and ceramic top coating due to mismatched thermal expansion and sintering effects, ultimately leading to coating degradation. Therefore, reducing the generation rate of large stresses in the coating, especially shear stresses, can effectively prevent the generation and propagation of transverse cracks and increase the thermal cycling life of TBCs.
materials science, ceramics