Microstructure and mechanical properties of thixoforged complex box-type component of 2A12 aluminum alloy

Jufu Jiang,Ying Zhang,Ying Wang,Guanfei Xiao,Yingze Liu,Li Zeng

DOI: https://doi.org/10.1016/j.matdes.2020.108859

2020-08-01

Abstract:<p>Complex box-type components of 2A12 aluminum alloy were thixoforged successfully, and their microstructures and mechanical properties were studied. Full filling status without surface defects was acquired by thixoforging a trapezoidal semisolid billet at the female die temperature of 420 °C and punch temperature of 340 °C. The maximum yield strength, ultimate tensile strength and elongation of the thixoforged component under optimized T4 treatment condition were 263.4 MPa, 414.2 MPa and 36.0%, respectively. Liquid segregation phenomenon happened at the upper edge of the component due to liquid flow and flow of liquid incorporating solid particles. Liquid fraction at the bottom part of the component was little, therefore severe plastic deformation mechanism of solid particles along with dynamic recrystallization was dominant. Dislocations, dislocation loops and dislocation bands of thixoforged 2A12 product were observed through transmission electron microscope (TEM). Deformation textures (Brass, Goss and S), recrystallization textures (Cube and R) and shear texture (rotated Cube) existed at the bottom region. Dispersoids Al₂₀Cu₂Mn₃, Al₇Cu₂Fe particles and intermetallic phase S (Al₂CuMg) were speculated in the microstructure of thixoforged 2A12 component with T4 heat treatment. Dislocations strengthening, refinement strengthening and strengthening of the second phase codetermined the final mechanical properties.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The paper aims to address the issues encountered in the semi-solid die forging process of complex box-shaped parts made of 2A12 aluminum alloy, specifically including:

1. **Improving Forming Quality**: Research how to achieve complete filling of complex-shaped 2A12 aluminum alloy box-shaped parts by optimizing parameters such as mold temperature and punch temperature, and avoid surface defects.
2. **Enhancing Mechanical Properties**: Explore how different heat treatment conditions (such as T4 treatment) can improve the yield strength, tensile strength, and elongation of complex box-shaped parts made of 2A12 aluminum alloy.
3. **Understanding Microstructure Evolution**: Analyze the microstructural changes of 2A12 aluminum alloy during the semi-solid die forging process, particularly the mechanisms of plastic deformation, dynamic recrystallization, and the formation of various textures (such as Brass, Goss, S, Cube, and R textures).

Through these studies, the authors hope to provide theoretical support and technical guidance for the semi-solid die forging process of complex box-shaped parts made of 2A12 aluminum alloy, thereby promoting its application in fields such as aerospace and robotics.