Steel Sheet Deformation in Clinch-Riveting Joining Process

Witkowski,Mucha,Boda

DOI: https://doi.org/10.3390/met14030367

IF: 2.695

2024-03-22

Metals

Abstract:This paper presents the deformation of a joined sheet after the clinch riveting process. The DX51D steel sheet with zinc coating was used. The samples to be joined with clinch riveting technology had a thickness of 1 ± 0.05 mm and 1.5 ± 0.1 mm. The sheet deformation was measured before and after the joining process. The rivet was pressed in the sheets with the same dimension between the rivet axis and three sheet edges: 20, 30, and 40 mm. For fixed segments of the die, from the rivet side close to the rivet, the sheet deformation was greater than that of the area with movable segments. The movement of the die's sliding element caused more sheet material to flow in the space between the fixed part of the die and movable segments. Hence, the sheet deformation in these places was smaller than for the die's fixed element—the sheet material was less compressed. For sheet thickness values of 1.5 mm and a width value of 20 mm, the bulk of the sheet was observed. For a sheet width of 20 mm, it was observed that the deformation of the upper and lower sheets in the area of the rivet was greater than for sheet width values of 30 or 40 mm.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily investigates the impact of different sheet widths and varying distances of the joint axis from the sheet edge on the deformation of connecting elements during the clinch-riveting process for metal sheets. Specifically:

- **Research Background**: In the manufacturing of thin-walled structures, despite continuous improvements in the design of machines and tools, unpredictable shape changes still occur during forming or connecting processes. This is particularly true for joints near the sheet edge, where their position significantly affects the shape and dimensional accuracy of thin-walled structures. Therefore, controlling deformation during these connecting processes is crucial.

- **Research Subject**: The materials used in the experiments are DX51D steel sheets with a zinc coating, with thicknesses of 1.0 mm and 1.5 mm.

- **Research Method**: By varying the sheet width (20 mm, 30 mm, and 40 mm) and the distance of the joint from the sheet edge, the deformation of the sheets under different conditions was studied. A clinch-riveting tool with a movable segment was used, and the deformation before and after the connection was measured.

- **Research Objective**: The aim is to analyze the degree of deformation of the sheets under different parameters, especially when the joint is close to the sheet edge, where deformation is more significant. Through experimental data, the researchers hope to identify the optimal connecting parameters to minimize unnecessary deformation.