Dielectric response and electromagnetic wave absorption of novel macroporous short carbon fibers/mullite composites

Lan Long,Jianxiong Xu,Heng Luo,Peng Xiao,Wei Zhou,Yang Li
DOI: https://doi.org/10.1111/jace.17401
IF: 4.186
2020-08-25
Journal of the American Ceramic Society
Abstract:<p>For wider‐band and stronger electromagnetic (EM) wave absorption, macroporous short carbon fibers/mullite matrix (C<sub>f</sub>/Mu) composites were prepared via introducing short carbon fibers (0, 0.7 and 1.3 vol%) with length of 2‐3 mm into macroporous mullite ceramic by gel‐casting. The density of as‐prepared C<sub>f</sub>/Mu composites decreases from 2.93 g/cm<sup>3</sup> to 2.74 g/cm<sup>3</sup>, while the porosity increases from 3.32% to 10.76% with the rise of carbon fibers content. The diameter of macropores in C<sub>f</sub>/Mu composites is ranging from several microns to tens of microns. Complex permittivity and dielectric loss of the prepared composites in X‐band (8.2‐12.4 GHz) are significantly enhanced with increased carbon fibers content. The best EM wave absorption performance is obtained in the macroporous C<sub>f</sub>/Mu composites containing only 0.7 vol% carbon fibers (C<sub>f</sub>/Mu‐0.7). The maximum absorption loss of C<sub>f</sub>/Mu‐0.7 is ‐38.3 dB at 12.08 GHz at the thickness of 2.1 mm, and effective absorption bandwidth below ‐10 dB (over 90% of EM wave absorption) covers the whole X band with the thickness of 2.35 mm. The results suggest that the C<sub>f</sub>/Mu composites can be promising high‐performance EM wave absorbing materials.</p>
materials science, ceramics
What problem does this paper attempt to address?